Growth and Investigation of Nd_{1-x}Sm_{x}ScO_{3} and Sm_{1-x}Gd_{x}ScO_{3} Solid-Solution Single Crystals
Authors:
R. Uecker,
D. Klimm,
R. Bertram,
M. Bernhagen,
I. Schulze-Jonack,
M. Brützam,
A. Kwasniewski,
Th. M. Gesing,
D. G. Schlom
Abstract:
The pseudo-cubic lattice parameters of rare-earth (RE) scandate, REScO3, single crystals grown by the Czochralski technique with RE=Dy to Pr lie between about 3.95 and 4.02 Angstrom. These crystals are the only available perovskite substrates in this lattice constant range that can withstand virtually any thin film growth conditions. Two members of this series, PmScO3 and EuScO3, are, however, not…
▽ More
The pseudo-cubic lattice parameters of rare-earth (RE) scandate, REScO3, single crystals grown by the Czochralski technique with RE=Dy to Pr lie between about 3.95 and 4.02 Angstrom. These crystals are the only available perovskite substrates in this lattice constant range that can withstand virtually any thin film growth conditions. Two members of this series, PmScO3 and EuScO3, are, however, not suitable for substrate applications. Because the pseudo-cubic lattice parameters between neighbouring REScO3 compounds decrease with rising atomic number of the RE in about 0.01 Angstrom steps, the unsuitability of PmScO3 (radioactivity) and EuScO3 (incompatibility with Si) causes an interruption in this lattice spacing sequence. To replace them, solid solutions of their adjacent rare-earth scandates, i.e., (Nd0.5Sm0.5)ScO3 and (Sm0.5Gd0.5)ScO3, were grown by the Czochralski method. Their average pseudo-cubic lattice parameters of 3.9979 Angstrom and 3.9784 Angstrom are very close to those of PmScO3 and EuScO3, respectively, and they show very low segregation. These qualities make these solid solutions excellent substitutes for PmScO3 and EuScO3.
△ Less
Submitted 10 June, 2013; v1 submitted 5 April, 2013;
originally announced April 2013.
Polar phonon anomalies in single crystalline TbScO3
Authors:
Stanislav Kamba,
Veronica Goian,
Dmitry Nuzhnyy,
Viktor Bovtun,
Martin Kempa,
Jan Prokleska,
Margitta Bernhagen,
Reinhard Uecker,
Darrell G. Schlom
Abstract:
Polarized infrared reflectivity spectra of a (110)-oriented TbScO3 single crystal plate were measured down to 10 K. The number of observed polar phonons active along the crystallographic c axis at low temperatures is much higher than predicted by factor-group analysis for the orthorhombic Pbnm space group. Moreover, the lowest frequency phonons active in E||c as well as in E||[1-10] polarized spec…
▽ More
Polarized infrared reflectivity spectra of a (110)-oriented TbScO3 single crystal plate were measured down to 10 K. The number of observed polar phonons active along the crystallographic c axis at low temperatures is much higher than predicted by factor-group analysis for the orthorhombic Pbnm space group. Moreover, the lowest frequency phonons active in E||c as well as in E||[1-10] polarized spectra exhibit dramatic softening tending to a lattice instability at low temperatures. The dielectric permittivity at microwave frequencies does not show any ferroelectric-like anomaly, but the dielectric loss exhibits a maximum at 100 K. The origin of the discrepancy between the number of predicted and observed polar phonons as well as the tendency toward lattice instability are discussed. Magnetic measurements reveal an antiferromagnetic phase transition near 3 K.
△ Less
Submitted 10 August, 2012;
originally announced August 2012.