Electronic structure property relationship in glassy Ti-Zr-Nb-(Cu,Ni,Co)
Authors:
Marko Kuveždić,
Emil Tafra,
Emil Babić,
Ramir Ristić,
Krešo Zadro,
Damir Starešinić,
Ignacio A. Figueroa,
Mario Basletić
Abstract:
In this work we revisit vast amount of existing data on physical properties of Ti-Zr-Nb-(Cu,Ni,Co) glassy alloys over a broad range of concentrations (from the high entropy range to that of conventional Cu-, Ni- or Co-rich alloys). By using our new approach based on total content of late transition metal(s), we derive a number of physical parameters of a hypothetical amorphous TiZrNb alloy: lattic…
▽ More
In this work we revisit vast amount of existing data on physical properties of Ti-Zr-Nb-(Cu,Ni,Co) glassy alloys over a broad range of concentrations (from the high entropy range to that of conventional Cu-, Ni- or Co-rich alloys). By using our new approach based on total content of late transition metal(s), we derive a number of physical parameters of a hypothetical amorphous TiZrNb alloy: lattice parameter $a = (3.42 \pm 0.02)$Å, Sommerfeld coefficient $γ= 6.2\,$mJ/mol$\,$K$^2$, density of states at $N(E_F) = 2.6\,(\text{at eV})^{-1}$, magnetic susceptibility $(2.00 \pm 0.05)\,$mJ/T$^2\,$mol, superconducting transition temperature $T_c = (8 \pm 1)\,$K, upper critical field $μ_0 H_{c2}(0) = (20 \pm 5)\,$T, and coherence length $ξ(0) = (40 \pm 3)\,$Å. We show that our extrapolated results for amorphous TiZrNb alloy would be similar to that of crystalline TiZrNb, except for superconducting properties (most notably the upper critical field $H_{c2}(0)$), which might be attributed to the strong topological disorder of the amorphous phase. Also, we offer an explanation of the discrepancy between the variations of $T_c$ with the average number of valency electrons in neighboring alloys of 4d transition metals and some high entropy alloys. Overall, we find that our novel method of systematic analysis of results is rather general, as it can provide reliable estimates of the properties of any alloy which has not been prepared as yet.
△ Less
Submitted 5 February, 2025;
originally announced February 2025.
-
Electronic structure-property relationship in an Al0.5TiZrPdCuNi high-entropy alloy
Authors:
Emil Babić,
Ignacio A. Figueroa,
Vesna Mikšić Trontl,
Petar Pervan,
Ivo Pletikosić,
Ramir Ristić,
Amra Salčinović Fetić,
Željko Skoko,
Damir Starešinić,
Tonica Valla,
Krešo Zadro
Abstract:
The valence band (VB) structure of an Al0.5TiZrPdCuNi high-entropy alloy (HEA) obtained from X-ray photoelectron spectroscopy has been compared to that recently calculated by Odbadrakh et al, 2019. Both experimental and theoretical VBs show split-band structures typical of alloys composed from the early (TE) and late (TL) transition metals. Accordingly, several properties of this alloy (both in th…
▽ More
The valence band (VB) structure of an Al0.5TiZrPdCuNi high-entropy alloy (HEA) obtained from X-ray photoelectron spectroscopy has been compared to that recently calculated by Odbadrakh et al, 2019. Both experimental and theoretical VBs show split-band structures typical of alloys composed from the early (TE) and late (TL) transition metals. Accordingly, several properties of this alloy (both in the glassy and crystalline state) associated with the electronic structure (ES), are compared with those of similar TE-TL alloys. The comparison shows in addition to the usual dependence on the total TL content strong effect of alloying with Al on the density of states at the Fermi level, N(EF) and on the magnetic susceptibility of Al0.5TiZrPdCuNi HEA, which is like that of conventional glassy alloys, such as Zr-Cu-Al ones. Despite some similarity between the shapes of theoretical and corresponding experimental VBs there are significant quantitative differences between them which should be taken into account in any future studies of ES in HEAs and other compositionally complex alloys (CCA).
△ Less
Submitted 16 February, 2024;
originally announced February 2024.
-
Comment on: High Mixing Entropy Enhanced Energy States in Metallic Glasses
Authors:
Ramir Ristić,
Emil Babić
Abstract:
A recent paper by Juntao Huo et al [Chin. Phys. Lett. 39 (2022) 0464011] reported a correlation between the entropy of mixing (and the corresponding energy state) and the thermal stability and mechanical parameters, for three Zr-Ti-Cu-Ni-Be metallic glasses (MG) including a high-entropy one (HEMG). The authors dismissed a possible compositional contribution to the variations of the thermal stabili…
▽ More
A recent paper by Juntao Huo et al [Chin. Phys. Lett. 39 (2022) 0464011] reported a correlation between the entropy of mixing (and the corresponding energy state) and the thermal stability and mechanical parameters, for three Zr-Ti-Cu-Ni-Be metallic glasses (MG) including a high-entropy one (HEMG). The authors dismissed a possible compositional contribution to the variations of the thermal stability and mechanical parameters studied.
△ Less
Submitted 1 May, 2022;
originally announced May 2022.
-
Transition from high-entropy to conventional $(TiZrNbCu)_{1-x}Co_x$ metallic glasses
Authors:
Ramir Ristić,
Ignacio A. Figueroa,
Amra Salčinović Fetić,
Krešo Zadro,
Vesna Mikšić Trontl,
Petar Pervan,
Emil Babić
Abstract:
A new amorphous alloy system $(TiZrNbCu)_{1-x}Co_x$ covering a broad composition range from the high-entropy (HEA) to Co rich alloys (x$\leqslant$ 0.43) has been fabricated, characterized and investigated. A comprehensive study of the chemical compositions, homogeneity, thermal stability, electronic structure and magnetic and mechanical properties has been performed. All properties change their va…
▽ More
A new amorphous alloy system $(TiZrNbCu)_{1-x}Co_x$ covering a broad composition range from the high-entropy (HEA) to Co rich alloys (x$\leqslant$ 0.43) has been fabricated, characterized and investigated. A comprehensive study of the chemical compositions, homogeneity, thermal stability, electronic structure and magnetic and mechanical properties has been performed. All properties change their variations with x within the HEA range. In particular, the average atomic volume deviates from the Vegard's law for x$\ge 0.2$, where also the average atomic packing fraction suddenly changes. The valence band structure, studied with ultraviolet photoemission spectroscopy, shows a split-band shape with 3d-states of Co approaching the Fermi level on increasing x. Due to onset of magnetic correlations magnetic susceptibility rapidly increases for x$\ge 0.25$. Very high microhardness increases rapidly with x. The results are compared with those for similar binary and quinary metallic glasses and with those for Cantor type of crystalline alloys.
△ Less
Submitted 17 July, 2021;
originally announced July 2021.
-
Change of electronic properties on transition from high-entropy to Ni-rich (TiZrNbCu)(1-x)Ni(x) alloys
Authors:
Marko Kuveždić,
Emil Tafra,
Mario Basletić,
Ramir Ristić,
Petar Pervan,
Vesna Mikšić Trontl,
Ignacio A Figueroa,
Emil Babić
Abstract:
We present results of comprehensive study of electronic properties of (TiZrNbCu)(1-x)Ni(x) metallic glasses performed in broad composition range x encompassing both, high entropy (HE) range, and conventional Ni-base alloy concentration range, x >= 0.35. The electronic structure studied by photoemission spectroscopy and low temperature specific heat (LTSH) reveal a split-band structure of density o…
▽ More
We present results of comprehensive study of electronic properties of (TiZrNbCu)(1-x)Ni(x) metallic glasses performed in broad composition range x encompassing both, high entropy (HE) range, and conventional Ni-base alloy concentration range, x >= 0.35. The electronic structure studied by photoemission spectroscopy and low temperature specific heat (LTSH) reveal a split-band structure of density of states inside valence band with d-electrons of Ti, Zr, Nb and also Ni present at Fermi level N(E_F), whereas LTSH and magnetoresistivity results show that variation of N(E_F) with x changes in Ni-base regime. The variation of superconducting transition temperatures with x closely follows that of N(E_F). The electrical resistivities of all alloys are high and decrease with increasing temperature over most of explored temperature range, and their temperature dependence seems dominated by weak localization effects over a broad temperature range (10-300 K). The preliminary study of Hall effect shows positive Hall coefficient that decreases rapidly in Ni-base alloys.
△ Less
Submitted 23 December, 2019;
originally announced December 2019.
-
Structure property relationship in $(TiZrNbCu)_{1-x}Ni_x$ metallic glasses
Authors:
Emil Babić,
Damir Pajić,
Krešo Zadro,
Katica Biljaković,
Vesna Mikšić Trontl,
Petar Pervan,
Damir Starešinić,
Ignacio A. Figueroa,
Ahmed Kuršumović,
Štefan Michalik,
Andrea Lachová,
György Remenyi,
Ramir Ristić
Abstract:
The atomic structure, electronic structure and physical properties of $(TiZrNbCu)_{(1-x)}Ni_x$ (x $\leq$ 0.5) metallic glasses (MG) were studied in both the high-entropy (0<x<0.35) and the higher Ni concentration range (x $\geq$ 0.35). Atomic structure studies performed with X-ray diffraction and synchrotron powder diffraction provided average atomic volumes, structure factors, radial distribution…
▽ More
The atomic structure, electronic structure and physical properties of $(TiZrNbCu)_{(1-x)}Ni_x$ (x $\leq$ 0.5) metallic glasses (MG) were studied in both the high-entropy (0<x<0.35) and the higher Ni concentration range (x $\geq$ 0.35). Atomic structure studies performed with X-ray diffraction and synchrotron powder diffraction provided average atomic volumes, structure factors, radial distribution functions, coordination numbers and packing densities. Electronic structure studies performed using photoemission spectroscopy and low-temperature specific heat provided information about the electronic density of states within the valence band and at the Fermi level and also about interatomic bonding and atomic vibrations (from the Debye temperature and the boson peak). Variations of both atomic structure and electronic structure with x showed a clear change for x $\geq$ 0.35, which corresponds to a valence electron number $\geq$ 7.4. All physical properties, namely thermal stability parameters, Debye temperatures, boson peaks, magnetic, elastic and electronic transport properties change their concentration-dependence for x$\geq$ 0.35. The results are compared with those for binary and ternary MGs of the same elements.
△ Less
Submitted 22 June, 2018;
originally announced June 2018.
-
Properties of $(TiZrNbCu)_{1-x}$$Ni_{x}$ Metallic Glasses
Authors:
Ignacio A. Figueroa,
Ramir Ristić,
Ahmed Kuršumović,
Katica Biljaković,
Damir Starešinić,
Damir Pajić,
György Remenyi,
Emil Babić
Abstract:
Recent studies (J. Alloys Compd. 695 (2017) 2661) of the electronic structure and properties of $(TiZrNbCu)_{1-x}$$Ni_{x}$ (x$\leq$0.25) amorphous high entropy alloys (a-HEA) have been extended to x=0.5 in order to compare behaviours of a-HEA and conventional Ni-base metallic glasses (MG). The amorphous state of all samples was verified by thermal analysis and X-ray diffraction (XRD). XRD indicate…
▽ More
Recent studies (J. Alloys Compd. 695 (2017) 2661) of the electronic structure and properties of $(TiZrNbCu)_{1-x}$$Ni_{x}$ (x$\leq$0.25) amorphous high entropy alloys (a-HEA) have been extended to x=0.5 in order to compare behaviours of a-HEA and conventional Ni-base metallic glasses (MG). The amorphous state of all samples was verified by thermal analysis and X-ray diffraction (XRD). XRD indicated a probable change in local atomic arrangements, i.e. short-range-order (SRO) for x$\geq$0.35. Simultaneously, thermal parameters, such as the first crystallization temperature $T_{x}$ and the liquidus temperature showed a tendency to saturate for x$\geq$0.35 . The same tendency also appeared in the magnetic susceptibility $χ_{exp}$ and the linear term in the low temperature specific heat γ. The Debye temperatures and Youngs moduli also tend to saturate for x$\geq$0.35. These unusual changes in SRO and all properties within the amorphous phase seem correlated with the change of valence electron number (VEC) on increasing x.
△ Less
Submitted 14 February, 2018; v1 submitted 21 August, 2017;
originally announced August 2017.
-
Electronic structure and glass forming ability in early and late transition metal alloys
Authors:
E. Babić,
R. Ristić,
I. A. Figueroa,
D. Pajić,
Ž. Skoko,
K. Zadro
Abstract:
A correlation between the change in magnetic susceptibility (Δ\c{hi}exp) upon crystallization of Cu-Zr, Hf metallic glasses (MG) with their glass forming ability (GFA) observed recently is found to apply to Cu-Ti and Zr-Ni alloys, too. In particular, a small Δ\c{hi}exp , which reflects similar electronic structures, ES, of glassy and corresponding crystalline alloys, corresponds to high GFA. Here,…
▽ More
A correlation between the change in magnetic susceptibility (Δ\c{hi}exp) upon crystallization of Cu-Zr, Hf metallic glasses (MG) with their glass forming ability (GFA) observed recently is found to apply to Cu-Ti and Zr-Ni alloys, too. In particular, a small Δ\c{hi}exp , which reflects similar electronic structures, ES, of glassy and corresponding crystalline alloys, corresponds to high GFA. Here, we studied Δ\c{hi}exp in five Cu-Ti and four Cu-Zr and Ni-Zr MGs. The fully crystalline final state of all alloys was verified from X-ray diffraction patterns. The variation of GFA with composition in Cu-Ti, Cu-Zr and Cu-Hf MGs was established from the variation of the corresponding critical casting thickness, dc. Due to the absence of data for dc in Ni-Zr MGs their GFA was described by using empirical criteria, such as the reduced glass transition temperature. A very good correlation between Δ\c{hi}exp and dc (and/or other criteria for GFA) was observed for all alloys studied. The correlation between the ES and GFA showed up best for Cu-Zr and NiZr2 alloys where direct data for the change in ES (ΔES) upon crystallization are available. The applicability of the Δ\c{hi}exp (ΔES) criterion for high GFA (which provides a simple way to select the compositions with high GFA) to other metal-metal MGs (including ternary and multicomponent bulk MGs) is briefly discussed.
△ Less
Submitted 19 December, 2017; v1 submitted 11 June, 2017;
originally announced June 2017.
-
Electronic structure and properties of (TiZrNbCu)_1-xNi_x high entropy amorphous alloys
Authors:
Katica Biljaković,
György Remenyi,
Ignacio A. Figueroa,
Ramir Ristić,
Damir Pajić,
Ahmed Kuršumović,
Damir Starešinić,
Krešo Zadro,
Emil Babić
Abstract:
A comprehensive study of selected properties of four (TiZrNbCu)_1-xNi_x (x \le 0.25) amorphous high entropy alloys (a-HEA) has been performed. The samples were ribbons about 20 \mum thick and their fully amorphous state was verified by X-ray diffraction and thermal analysis. The surface morphology, precise composition and the distribution of components were studied with a Scanning electron microsc…
▽ More
A comprehensive study of selected properties of four (TiZrNbCu)_1-xNi_x (x \le 0.25) amorphous high entropy alloys (a-HEA) has been performed. The samples were ribbons about 20 \mum thick and their fully amorphous state was verified by X-ray diffraction and thermal analysis. The surface morphology, precise composition and the distribution of components were studied with a Scanning electron microscope (SEM) with an energy dispersive spectroscopy (EDS) attachment. The properties selected were the melting temperature (T_m), the low temperature specific heat (LTSH), the magnetic susceptibility χ_exp and the Young^,s modulus (E). Whereas LTSH and χ_exp were measured for the as-cast samples, E was measured both for as-cast samples and relaxed samples (after a short anneal close to the glass transition temperature). The LTSH showed that the electronic density of states at the Fermi level, N_0(E_F), decreases with increasing x, whereas the Debye temperature (θ_D) increases with x. This is similar to what is observed in binary and ternary amorphous alloys of early transition metals (TE) with late transition metals (TL) and indicates that N_0(E_F) is dominated by the d-electrons of the TE. The LTSH also showed the absence of superconductivity down to 1.8K and indicated the emergence of the Boson peak above 4K in all alloys.The free-electron like paramagnetic contribution to χ_exp also decreases with x, whereas E, like θ_D, increases with x, indicating enhanced interatomic bonding on addition of Ni. The applicability of the rule of mixtures to these and other similar HEAs is briefly discussed.
△ Less
Submitted 18 November, 2016;
originally announced November 2016.
-
On the origin of bulk glass forming ability in Cu-Hf, Zr alloys
Authors:
Ramir Ristić,
Krešo Zadro,
Damir Pajić,
Ignacio A. Figueroa,
Emil Babić
Abstract:
Understanding the formation of bulk metallic glasses (BMG) in metallic systems and finding a reliable criterion for selection of BMG compositions are among the most important issues in condensed matter physics and material science. Using the results of magnetic susceptibility measurements performed on both amorphous and crystallized Cu-Hf alloys (30-70 at% Cu) we find a correlation between the dif…
▽ More
Understanding the formation of bulk metallic glasses (BMG) in metallic systems and finding a reliable criterion for selection of BMG compositions are among the most important issues in condensed matter physics and material science. Using the results of magnetic susceptibility measurements performed on both amorphous and crystallized Cu-Hf alloys (30-70 at% Cu) we find a correlation between the difference in magnetic susceptibilities of corresponding glassy and crystalline alloys and the variation in the glass forming ability (GFA) in these alloys. Since the same correlation can be inferred from data for the properties associated with the electronic structure of Cu-Zr alloys, it seems quite general and may apply to other glassy alloys based on early and late transition metals. This correlation is plausible from the free energy considerations and provides a simple way to select the compositions with high GFA.
△ Less
Submitted 25 April, 2016; v1 submitted 27 January, 2016;
originally announced January 2016.
-
Correlation between doping induced disorder and superconducting properties in carbohydrate doped MgB2
Authors:
J. H. Kim,
S. X. Dou,
Sangjun Oh,
M. Jercinovic,
E. Babic,
T. Nakane,
H. Kumakura
Abstract:
A comprehensive study of the effects of carbohydrate doping on the superconductivity of MgB2 has been conducted. In accordance with the dual reaction model, more carbon substitution is achieved at lower sintering temperature. As the sintering temperature is lowered, lattice disorder is increased. Disorder is an important factor determining the transition temperature for the samples studied in th…
▽ More
A comprehensive study of the effects of carbohydrate doping on the superconductivity of MgB2 has been conducted. In accordance with the dual reaction model, more carbon substitution is achieved at lower sintering temperature. As the sintering temperature is lowered, lattice disorder is increased. Disorder is an important factor determining the transition temperature for the samples studied in this work, as evidenced from the correlations among the lattice strain, the resistivity and the transition temperature. It is further shown that the increased critical current density in the high field region can be understood by a recently-proposed percolation model [Phys. Rev. Lett. 90 (2003) 247002]. For the critical current density analysis, the upper critical field is estimated from a correlation that has been reported in a recent review article [Supercond. Sci. Technol. 20 (2007) R47], where a sharp increase in the upper critical field by doping is mainly due to an increase in lattice disorder or impurity scattering. On the other hand, it is shown that the observed reduction in self-field critical current density is related to the reduction in the pinning force density by carbohydrate doping.
△ Less
Submitted 8 October, 2008;
originally announced October 2008.
-
Enhanced superconductivity in Hf-base metallic glasses
Authors:
Emil Tafra,
Mario Basletic,
Ramir Ristic,
Emil Babic,
Amir Hamzic
Abstract:
Systematic study of electrical resistivity of Hf_{100-x}Fe_x (x=20,25), Hf_{100-x}Cu_x (x=30,40,50), and Ti_{65}Cu_{35} metallic glasses has been done in the temperature range 0.3 K - 290 K, and in magnetic fields B <= 5 T. All Hf-base alloys are superconducting with T_c >= 0.44 K, which is well above T_c of pure crystalline Hf (0.13 K). From the initial slopes of the upper critical fields, (dH_…
▽ More
Systematic study of electrical resistivity of Hf_{100-x}Fe_x (x=20,25), Hf_{100-x}Cu_x (x=30,40,50), and Ti_{65}Cu_{35} metallic glasses has been done in the temperature range 0.3 K - 290 K, and in magnetic fields B <= 5 T. All Hf-base alloys are superconducting with T_c >= 0.44 K, which is well above T_c of pure crystalline Hf (0.13 K). From the initial slopes of the upper critical fields, (dH_{c2}/dT)_{T_c}, and resistivities we determined the dressed electronic densities of states, N_γ(E_F), for all alloys. Both T_c and N_γ(E_F) decrease with increasing x (Fe and Cu content). The results are compared with those for corresponding Zr-base metallic glasses and ion-implanted Hf films.
△ Less
Submitted 26 September, 2008; v1 submitted 3 June, 2008;
originally announced June 2008.
-
Mechanism of enhancement of electromagnetic properties of MgB2 by nano-SiC doping
Authors:
S. X. Dou,
O. Shcherbakova,
W. K. Yeoh,
J. H. Kim,
S. Soltanian,
X. L. Wang,
C. Senatore,
R. Flukiger,
M. Dhalle,
O. Husnjak,
E. Babic
Abstract:
A comparative study of pure, SiC, and C doped MgB2 wires has revealed that the SiC doping allowed C substitution and MgB2 formation to take place simultaneously at low temperatures. C substitution enhances Hc2, while the defects, small grain size and nanoinclusions induced by C incorporation and low temperature processing are responsible for the improvement in Jc. The irreversibility field (Hirr…
▽ More
A comparative study of pure, SiC, and C doped MgB2 wires has revealed that the SiC doping allowed C substitution and MgB2 formation to take place simultaneously at low temperatures. C substitution enhances Hc2, while the defects, small grain size and nanoinclusions induced by C incorporation and low temperature processing are responsible for the improvement in Jc. The irreversibility field (Hirr) for the SiC doped sample reached the benchmarking value of 10 T at 20 K, exceeding that of NbTi at 4.2 K. This dual reaction model also enables us to predict desirable dopants for enhancing the performance properties of MgB2.
△ Less
Submitted 1 March, 2007; v1 submitted 16 January, 2007;
originally announced January 2007.
-
Thermal relaxation of magnetic clusters in amorphous Hf_{57}Fe_{43} alloy
Authors:
Damir Pajic,
Kreso Zadro,
Ramir Ristic,
Ivica Zivkovic,
Zeljko Skoko,
Emil Babic
Abstract:
The magnetization processes in binary magnetic/nonmagnetic amorphous alloy Hf_{57}Fe_{43} are investigated by the detailed measurements of magnetic hysteresis loops, temperature dependence of magnetization, relaxation of magnetization and magnetic ac susceptibility, including a nonlinear term. Blocking of magnetic moments at lower temperatures is accompanied with the slow relaxation of magnetiza…
▽ More
The magnetization processes in binary magnetic/nonmagnetic amorphous alloy Hf_{57}Fe_{43} are investigated by the detailed measurements of magnetic hysteresis loops, temperature dependence of magnetization, relaxation of magnetization and magnetic ac susceptibility, including a nonlinear term. Blocking of magnetic moments at lower temperatures is accompanied with the slow relaxation of magnetization and magnetic hysteresis loops. All of the observed properties are explained with the superparamagnetic behaviour of the single domain magnetic clusters inside the nonmagnetic host, their blocking by the anisotropy barriers and thermal fluctuation over the barriers accompanied by relaxation of magnetization. From magnetic viscosity analysis based on thermal relaxation over the anisotropy barriers it is found out that magnetic clusters occupy the characteristic volume from 25 up to 200 nm3 . The validity of the superparamagnetic model of Hf_{57}Fe_{43} is based on the concentration of iron in the Hf_{100-x}Fe_{43} system that is just below the threshold for the long range magnetic ordering. This work throws more light on magnetic behaviour of other amorphous alloys, too.
△ Less
Submitted 19 June, 2007; v1 submitted 14 August, 2006;
originally announced August 2006.
-
Correlated vortex pinning in Si-nanoparticle doped MgB2
Authors:
I. Kusevic,
E. Babic,
O. Husnjak,
S. Soltanian,
X. L. Wang,
S. X. Dou
Abstract:
The magnetoresistivity and critical current density of well characterized Si-nanoparticle doped and undoped Cu-sheathed MgB$_{2}$ tapes have been measured at temperatures $T\geq 28$ K in magnetic fields $B\leq 0.9$ T. The irreversibility line $B_{irr}(T)$ for doped tape shows a stepwise variation with a kink around 0.3 T. Such $B_{irr}(T)$ variation is typical for high-temperature superconductor…
▽ More
The magnetoresistivity and critical current density of well characterized Si-nanoparticle doped and undoped Cu-sheathed MgB$_{2}$ tapes have been measured at temperatures $T\geq 28$ K in magnetic fields $B\leq 0.9$ T. The irreversibility line $B_{irr}(T)$ for doped tape shows a stepwise variation with a kink around 0.3 T. Such $B_{irr}(T)$ variation is typical for high-temperature superconductors with columnar defects (a kink occurs near the matching field $% B_φ$) and is very different from a smooth $B_{irr}(T)$ variation in undoped MgB$_{2}$ samples. The microstructure studies of nanoparticle doped MgB$_{2}$ samples show uniformly dispersed nanoprecipitates, which probably act as a correlated disorder. The observed difference between the field variations of the critical current density and pinning force density of the doped and undoped tape supports the above findings.
△ Less
Submitted 18 November, 2003;
originally announced November 2003.
-
Enhancement of Flux Pinning in Neutron Irradiated MgB$_{2}$ Superconductor
Authors:
E. Babic,
Dj. Miljanic,
K. Zadro,
I. Kusevic,
Z. Marohnic,
Dj. Drobac,
X. L. Wang,
S. X. Dou
Abstract:
m-H loops for virgin and neutron irradiated bulk and powder samples of MgB_{2} were measured in the temperature range 5-30 K in magnetic field B<= 1 T. The irradiation at thermal neutron fluences 9*10^{13} and 4.5*10^{14} cm^{-2} caused very small enhancement of m-H loops at lower temperatures (T<20 K), whereas the effect at high temperatures was unclear due to difficulty in achieving exactly th…
▽ More
m-H loops for virgin and neutron irradiated bulk and powder samples of MgB_{2} were measured in the temperature range 5-30 K in magnetic field B<= 1 T. The irradiation at thermal neutron fluences 9*10^{13} and 4.5*10^{14} cm^{-2} caused very small enhancement of m-H loops at lower temperatures (T<20 K), whereas the effect at high temperatures was unclear due to difficulty in achieving exactly the same measurement temperature prior and after irradiation. However, the irradiation at 4.5*10^{15} cm^{-2} produced clear enhancement of m-H loops (hence J_{c}) at all investigated temperatures, which provides the evidence for the enhancement of flux pinning in MgB_{2} due to ion tracks resulting from n+^{10}B reaction. The potential of this technique for the enhancement of flux pinning in high temperature superconductors is briefly discussed.
△ Less
Submitted 10 December, 2001;
originally announced December 2001.
-
High transport critical current density above 30 K in pure Fe-clad MgB2 tape
Authors:
S. Soltanian,
X. L. Wang,
I. Kusevic,
E. Babic,
A. H. Li,
H. K. Liu,
E. W. Collings,
S. X. Dou
Abstract:
Fe-clad MgB2 long tapes have been fabricated using a powder-in-tube technique. An Mg + 2B mixture was used as the central conductor core and reacted in-situ to form MgB2. The tapes were sintered in pure Ar at 800 ^(o) C for 1 h at ambient pressure. SEM shows a highly dense core with a large grain size of 100 micron. The Fe clad tape shows a sharp transition with transition width of 0.2 K and Tc0…
▽ More
Fe-clad MgB2 long tapes have been fabricated using a powder-in-tube technique. An Mg + 2B mixture was used as the central conductor core and reacted in-situ to form MgB2. The tapes were sintered in pure Ar at 800 ^(o) C for 1 h at ambient pressure. SEM shows a highly dense core with a large grain size of 100 micron. The Fe clad tape shows a sharp transition with transition width of 0.2 K and Tc0 at 37.5 K. We have achieved the highest transport critical current reported so far at 1.6 times 10^(4) A/cm^2 for both 29.5 K in 1 Tesla and 33 K in null field. R-T and critical current were also measured for fields perpendicular and parallel to the tape plane. The iron cladding shielded on the core from the applied external field, with the shielding being less effective for the field in the tape plane. Fe cladding may be advantageous for some applications as it could reduce the effects of both the self-field and external fields.
△ Less
Submitted 7 May, 2001;
originally announced May 2001.