Improved thermal stability in doped MnN/CoFe exchange bias systems
Authors:
Mareike Dunz,
Björn Büker,
Markus Meinert
Abstract:
We investigated the influence of doping antiferromagnetic MnN in polycrystalline MnN/CoFe exchange bias systems, showing high exchange bias of up to 1800 Oe at room temperature. The thermal stability of those systems is limited by nitrogen diffusion that occurs during annealing processes. In order to improve the thermal stability, defect energies of elements throughout the periodic table substitut…
▽ More
We investigated the influence of doping antiferromagnetic MnN in polycrystalline MnN/CoFe exchange bias systems, showing high exchange bias of up to 1800 Oe at room temperature. The thermal stability of those systems is limited by nitrogen diffusion that occurs during annealing processes. In order to improve the thermal stability, defect energies of elements throughout the periodic table substituting Mn were calculated via density functional theory. Elements calculated to have negative defect energies bind nitrogen stronger to the lattice and could be able to prevent diffusion. We prepared exchange bias stacks with doping concentrations of a few percent by (reactive) co-sputtering, testing doping elements with defect energies ranging from highly negative to slightly positive. We show that doping with elements calculated to have negative defect energies indeed improves the thermal stability. Y doped MnN layers with doping concentrations below 2% result in systems that show exchange bias fields higher than 1000 Oe for annealing temperatures up to 485° C.
△ Less
Submitted 9 August, 2018;
originally announced August 2018.
Large exchange bias in polycrystalline MnN/CoFe bilayers at room temperature
Authors:
Markus Meinert,
Björn Büker,
Dominik Graulich,
Mareike Dunz
Abstract:
We report on the new polycrystalline exchange bias system MnN/CoFe, which shows exchange bias of up to 1800Oe at room temperature with a coercive field around 600Oe. The room temperature values of the interfacial exchange energy and the effective uniaxial anisotropy are estimated to be $J_\mathrm{eff} = 0.41\,\mathrm{mJ}/\mathrm{m}^2$ and $K_\mathrm{eff} = 37\,\mathrm{kJ}\,/\,\mathrm{m}^3$. The th…
▽ More
We report on the new polycrystalline exchange bias system MnN/CoFe, which shows exchange bias of up to 1800Oe at room temperature with a coercive field around 600Oe. The room temperature values of the interfacial exchange energy and the effective uniaxial anisotropy are estimated to be $J_\mathrm{eff} = 0.41\,\mathrm{mJ}/\mathrm{m}^2$ and $K_\mathrm{eff} = 37\,\mathrm{kJ}\,/\,\mathrm{m}^3$. The thermal stability was found to be tunable by controlling the nitrogen content of the MnN. The maximum blocking temperature exceeds $325^\circ$C, however the median blocking temperature in the limit of thick MnN is $160^\circ$C. Good oxidation stability through self-passivation was observed, enabling the use of MnN in lithographically defined microstructures. As a proof-of-principle we demonstrate a simple GMR stack exchange biased with MnN, which shows clear separation between parallel and antiparallel magnetic states. These properties come along with a surprisingly simple manufacturing process for the MnN films.
△ Less
Submitted 18 September, 2015; v1 submitted 21 January, 2015;
originally announced January 2015.