Thermal activation energy of 3D vortex matter in NaFe1-xCoxAs (x=0.01, 0.03 and 0.07) single crystals
Authors:
W. J. Choi,
Y. I. Seo,
D. Ahmad,
Yong Seung Kwon
Abstract:
We report on the thermally activated flux flow dependency on the doping dependent mixed state in NaFe1-xCoxAs (x=0.01, 0.03, and 0.07) crystals using the magnetoresistivity in the case of B//c-axis and B//ab-plane. It was found clearly that irrespective of the doping ratio, magnetoresistivity showed a distinct tail just above the Tc, offset associated with the thermally activated flux flow (TAFF)…
▽ More
We report on the thermally activated flux flow dependency on the doping dependent mixed state in NaFe1-xCoxAs (x=0.01, 0.03, and 0.07) crystals using the magnetoresistivity in the case of B//c-axis and B//ab-plane. It was found clearly that irrespective of the doping ratio, magnetoresistivity showed a distinct tail just above the Tc, offset associated with the thermally activated flux flow (TAFF) in our crystals. Furthermore, in TAFF region the temperature dependence of the activation energy follows the relation U(T, B)=U_0 (B) (1-T/T_c )^q with q=1.5 in all studied crystals. The magnetic field dependence of the activation energy follows a power law of U_0 (B)~B^(-α) where the exponent α is changed from a low value to a high value at a crossover field of B=~2T, indicating the transition from collective to plastic pinning in the crystals. Finally, it is suggested that the 3D vortex phase is the dominant phase in the low-temperature region as compared to the TAFF region in our series samples.
△ Less
Submitted 27 June, 2017;
originally announced June 2017.
-
Fluctuation magnetoconductivity in pristine and protonirradiated Ca8.5La1.5(Pt3As8)(Fe2As2)5 single crystals
Authors:
D. Ahmad,
Y. I. Seo,
W. J. Choi,
Yong Seung Kwon
Abstract:
The influence of the proton irradiation on the thermally fluctuation-induced conductivity in Ca8.5La1.5(pt3As8)(Fe2As2)5 single crystal was investigatyed. The in-plane magnetoconductivity was measured up to H=13T. It is observed that the Tc was suppressed up to 30.3 from 32.5 K when the proton is irradiated whereas the amplitude of the fluctuation effect is the almost same in both samples. The res…
▽ More
The influence of the proton irradiation on the thermally fluctuation-induced conductivity in Ca8.5La1.5(pt3As8)(Fe2As2)5 single crystal was investigatyed. The in-plane magnetoconductivity was measured up to H=13T. It is observed that the Tc was suppressed up to 30.3 from 32.5 K when the proton is irradiated whereas the amplitude of the fluctuation effect is the almost same in both samples. The results were analyzed by the Ullah and Dorsey scaling functions based on the Hartree approximation to the Ginzburg-Landau free energy, including the critical-fluctuation regime. In the pristine sample, the 3D-2D crossover in the fluctuation effect was observed near the Tc. When the 3D-2D occurs, it is newly found that there is a regime simultaneously described by 2D and 3D fluctuation behaviors. Meanwhile, the proton-irradiated sample showed the 3D fluctuation.
△ Less
Submitted 29 September, 2016;
originally announced September 2016.
-
A ferromagnetic-like phase transition in new oxychalcogenide HgOCuSe
Authors:
G. C. Kim,
M. Cheon,
I. S. Park,
D. Ahmad,
Y. C. Kim
Abstract:
We report the synthesis of a new oxychalcogenide HgOCuSe sample. The resistivity decreases as a function of $T^{1.75}$ with decreasing temperature from room temperature down to around 80 K. There exists a very sharp ferromagnetic-like phase transition at around 60 K under a field of $H$ = 100 Oe. Contrary to the usual ferromagnetic materials, the descending and ascending branches of the magnetic h…
▽ More
We report the synthesis of a new oxychalcogenide HgOCuSe sample. The resistivity decreases as a function of $T^{1.75}$ with decreasing temperature from room temperature down to around 80 K. There exists a very sharp ferromagnetic-like phase transition at around 60 K under a field of $H$ = 100 Oe. Contrary to the usual ferromagnetic materials, the descending and ascending branches of the magnetic hysteresis curve, at 30 K, are reversed in the whole irreversible field range and the reverse irreversibility decreases at 5 K.
△ Less
Submitted 30 May, 2011;
originally announced May 2011.