Formation of Core-Shell Precipitates in off-stochiometric Ni-Mn-Sn Heusler alloys probed through the induced Sn-moment
Authors:
Benedikt Eggert,
Aslı Çakır,
Damian Günzing,
Nicolas Josten,
Franziska Scheibel,
Richard A. Brand,
Michael Farle,
Mehmet Acet,
Heiko Wende,
Katharina Ollefs
Abstract:
The Shell-ferromagnetic effect originates from the segregation process in off-stochiometric Ni-Mn-based Heusler. In this work, we investigate the precipitation process of L2$_1$-ordered Ni$_2$MnSn and L1$_0$-ordered NiMn in off-stochiometric Ni$_{50}$Mn$_{45}$Sn$_{5}$ during temper annealing, by X-ray diffraction (XRD) and $^{119}$Sn Mössbauer spectroscopy. While XRD probes long-range ordering of…
▽ More
The Shell-ferromagnetic effect originates from the segregation process in off-stochiometric Ni-Mn-based Heusler. In this work, we investigate the precipitation process of L2$_1$-ordered Ni$_2$MnSn and L1$_0$-ordered NiMn in off-stochiometric Ni$_{50}$Mn$_{45}$Sn$_{5}$ during temper annealing, by X-ray diffraction (XRD) and $^{119}$Sn Mössbauer spectroscopy. While XRD probes long-range ordering of the lattice structure, Mössbauer spectroscopy probes nearest-neighbour interactions, reflected in the induced Sn magnetic moment. As shown in this work, the induced magnetic Sn moment can be used as a detector for microscopic structural changes and is, therefore, a powerful tool for investigating the formation of nano-precipitates. Similar research can be performed in the future, for example, on different pinning type magnets like Sm-Co or Nd-Fe-B.
△ Less
Submitted 6 April, 2023;
originally announced April 2023.
-
Annealing time, temperature, and field dependence of pinned magnetic moments in the collinear antiferromagnet PdMn
Authors:
Nicolas Josten,
Olga Miroshkina,
Mehmet Acet,
Markus Gruner,
Michael Farle
Abstract:
Magnetic annealing of the collinear antiferromagnet PdMn with excess Pd produces strongly pinned magnetic moments in the annealing field direction. This behaviour can be understood with the help of the magnetic-field-biased diffusion model. Here, the magnetic field creates an energy difference between the two possible occupations of the antiferromagnetic Mn-sublattices by the Pd-excess atoms. This…
▽ More
Magnetic annealing of the collinear antiferromagnet PdMn with excess Pd produces strongly pinned magnetic moments in the annealing field direction. This behaviour can be understood with the help of the magnetic-field-biased diffusion model. Here, the magnetic field creates an energy difference between the two possible occupations of the antiferromagnetic Mn-sublattices by the Pd-excess atoms. This, mediated by diffusion, leads to an imbalance in the amount of the Pd-excess atoms in these sublattices and, subsequently, to an imbalance in the total magnetization of the sublattices. We investigate this effect's dependence on the annealing field, time, and temperature. The results are then compared to the results of the magnetic-field-biased diffusion model, which gives good agreement.
△ Less
Submitted 6 March, 2023;
originally announced March 2023.
-
Emergence of net magnetization by magnetic-field-biased diffusion in antiferromagnetic L1$_0$ NiMn
Authors:
Nicolas Josten,
Olga Miroshkina,
Sakia Noorzayee,
Benjamin Zingsem,
Aslı Çakır,
Mehmet Acet,
Ulf Wiedwald,
Markus Gruner,
Michael Farle
Abstract:
NiMn is a collinear antiferromagnet with high magneto crystalline anisotropy ($K_2=-9.7\times10^5\;\text{J m}^{-3}$). Through magnetic annealing of NiMn with excess Ni, strongly pinned magnetic moments emerge due to an imbalance in the distribution of Ni in the antiferromagnetic Mn-sublattices. The results are explained with a model of magnetic-field-biased diffusion, supported by ab initio calcul…
▽ More
NiMn is a collinear antiferromagnet with high magneto crystalline anisotropy ($K_2=-9.7\times10^5\;\text{J m}^{-3}$). Through magnetic annealing of NiMn with excess Ni, strongly pinned magnetic moments emerge due to an imbalance in the distribution of Ni in the antiferromagnetic Mn-sublattices. The results are explained with a model of magnetic-field-biased diffusion, supported by ab initio calculations. Another observation is the oxidation of Mn at the surface, causing an enrichment of Ni in the sub-surface region. This leads to an additional ferromagnetic response appearing in the magnetization measurements, which can be removed by surface polishing.
△ Less
Submitted 26 February, 2023;
originally announced February 2023.
-
Strain glass versus antisite disorder induced ferromagnetic state in Fe doped Ni-Mn-In Heusler martensites
Authors:
Rukma Nevgi,
K. R. Priolkar,
Mehmet Acet
Abstract:
Fe doping in Ni$_2$Mn$_{1.5}$In$_{0.5}$ results in suppression of the martensitic phase via two contrasting routes. In Ni$_2$Mn$_{1.5-x}$Fe$_{x}$In$_{0.5}$, the martensitic phase is converted to a strain glassy phase, while in Ni$_{2-y}$Fe$_y$Mn$_{1.5}$In$_{0.5}$, a cubic ferromagnetic phase results at the expense of the martensite. Careful studies of magnetic and structural properties reveal the…
▽ More
Fe doping in Ni$_2$Mn$_{1.5}$In$_{0.5}$ results in suppression of the martensitic phase via two contrasting routes. In Ni$_2$Mn$_{1.5-x}$Fe$_{x}$In$_{0.5}$, the martensitic phase is converted to a strain glassy phase, while in Ni$_{2-y}$Fe$_y$Mn$_{1.5}$In$_{0.5}$, a cubic ferromagnetic phase results at the expense of the martensite. Careful studies of magnetic and structural properties reveal the presence of the impurity $γ-$(Fe,Ni) phase as the reason for the emergence of non-ergodic strain glassy phase when Fe is sought to be doped at Y/Z (Mn) sites of X$_2$YZ Heusler alloy. Whereas attempts to dope Fe in the X (Ni) sublattice result in an A2 type antisite disorder that promotes a ferromagnetic ground state.
△ Less
Submitted 23 February, 2021;
originally announced February 2021.
-
Importance of site occupancy and absence of strain glassy phase in Ni$_{2-x}$Fe$_{x}$Mn$_{1.5}$In$_{0.5}$
Authors:
R. Nevgi,
Gangadhar Das,
M. Acet,
K. R. Priolkar
Abstract:
Martensitic transition temperature steadily decreases in Ni$_{2-x}$Fe$_{x}$Mn$_{1.5}$In$_{0.5}$ and is completely suppressed at $x$ = 0.2. Despite suppression of martensitic transition, Ni$_{1.8}$Fe$_{0.2}$Mn$_{1.5}$In$_{0.5}$ does not display the expected strain glassy phase. Instead, a ground state with dominant ferromagnetic interactions is observed. A study of structural and magnetic propertie…
▽ More
Martensitic transition temperature steadily decreases in Ni$_{2-x}$Fe$_{x}$Mn$_{1.5}$In$_{0.5}$ and is completely suppressed at $x$ = 0.2. Despite suppression of martensitic transition, Ni$_{1.8}$Fe$_{0.2}$Mn$_{1.5}$In$_{0.5}$ does not display the expected strain glassy phase. Instead, a ground state with dominant ferromagnetic interactions is observed. A study of structural and magnetic properties of $x$ = 0.2 reveal that the alloy consists of a major Fe rich cubic phase and a minor Fe deficient monoclinic phase favoring a ferromagnetic ground state. This is exactly opposite of that observed in Ni$_2$Mn$_{1-y}$Fe$_{y}$In$_{0.5}$ wherein a strain glassy phase is observed for $y$ = 0.1. The change in site symmetry of Fe when doped for Ni in contrast to Mn in the Heusler composition seems to support the growth of the ferromagnetic phase.
△ Less
Submitted 1 April, 2020;
originally announced April 2020.
-
Neutron diffraction and symmetry analysis of the martensitic transformation in Co-doped Ni$_2$MnGa
Authors:
Fabio Orlandi,
Aslı Çakır,
Pascal Manuel,
Dmitry D. Khalyavin,
Mehmet Acet,
Lara Righi
Abstract:
Martensitic transformations are strain driven displacive transitions governing the mechanical and physical properties in intermetallic materials. This is the case in Ni$_2$MnGa, where the martensite transition is at the heart of the striking magnetic shape memory and magneto-caloric properties. Interestingly, the martensitic transformation is preceded by a pre-martensite phase, and the role of thi…
▽ More
Martensitic transformations are strain driven displacive transitions governing the mechanical and physical properties in intermetallic materials. This is the case in Ni$_2$MnGa, where the martensite transition is at the heart of the striking magnetic shape memory and magneto-caloric properties. Interestingly, the martensitic transformation is preceded by a pre-martensite phase, and the role of this precursor and its influence on the martensitic transition and properties is still a matter of debate. In this work, we report on the influence of Co doping (Ni$_{50-x}$Co$_x$Mn$_{25}$Ga$_{25}$ with x = 3 and 5) on the martensitic transformation path in stoichiometric Ni$_2$MnGa by neutron diffraction. The use of the superspace formalism to describe the crystal structure of the modulated martensitic phases, joined with a group theoretical analysis allows unfolding the different distortions featuring the structural transitions. Finally, a general Landau thermodynamic potential of the martensitic transformation, based on the symmetry analysis is outlined. The combined use of phenomenological and crystallographic studies highlights the close relationship between the lattice distortions at the core of the Ni$_2$MnGa physical properties and, more in general, on the properties of the martensitic transformations in the Ni-Mn based Heusler systems.
△ Less
Submitted 18 March, 2020;
originally announced March 2020.
-
Dynamics of the magnetoelastic phase transition and adiabatic temperature change in Mn1.3Fe0.7P0.5Si0.55
Authors:
M. Fries,
T. Gottschall,
F. Scheibel,
L. Pfeuffer,
K. P. Skokov,
I. Skourski,
M. Acet,
M. Farle,
J. Wosnitza,
O. Gutfleisch
Abstract:
The adiabatic temperature change DTad of a Mn1.3Fe0.7P0.5Si0.55 Fe2P-type alloy was measured under different magnetic field-sweep rates from 0.93 Ts-1 to 2870 Ts-1. We find a field-sweep-rate independent magnetocaloric effect due to a partial alignment of magnetic moments in the paramagnetic region overlapping with the magnetocaloric effect of the first-order phase transition. Additionally, the fi…
▽ More
The adiabatic temperature change DTad of a Mn1.3Fe0.7P0.5Si0.55 Fe2P-type alloy was measured under different magnetic field-sweep rates from 0.93 Ts-1 to 2870 Ts-1. We find a field-sweep-rate independent magnetocaloric effect due to a partial alignment of magnetic moments in the paramagnetic region overlapping with the magnetocaloric effect of the first-order phase transition. Additionally, the first-order phase transition is not completed even in fields up to 20 T leading to a non-saturating behavior of DTad. Measurements in different pulsed fields reveal that the first-order phase transition cannot follow the fast field changes as previously assumed, resulting in a distinct field-dependent hysteresis in DTad.
△ Less
Submitted 4 July, 2019;
originally announced July 2019.
-
Evidence for the formation of nanoprecipitates with magnetically disordered regions in bulk $\mathrm{Ni}_{50}\mathrm{Mn}_{45}\mathrm{In}_{5}$ Heusler alloys
Authors:
Giordano Benacchio,
Ivan Titov,
Artem Malyeyev,
Inma Peral,
Mathias Bersweiler,
Philipp Bender,
Denis Mettus,
Dirk Honecker,
Elliot Paul Gilbert,
Mauro Coduri,
Andre Heinemann,
Sebastian Mühlbauer,
Asli Cakir,
Mehmet Acet,
Andreas Michels
Abstract:
Shell ferromagnetism is a new functional property of certain Heusler alloys which has been recently observed in $\mathrm{Ni}_{50}\mathrm{Mn}_{45}\mathrm{In}_{5}$. We report the results of a comparative study of the magnetic microstructure of bulk $\mathrm{Ni}_{50}\mathrm{Mn}_{45}\mathrm{In}_{5}$ Heusler alloys using magnetometry, synchrotron x-ray diffraction, and magnetic small-angle neutron scat…
▽ More
Shell ferromagnetism is a new functional property of certain Heusler alloys which has been recently observed in $\mathrm{Ni}_{50}\mathrm{Mn}_{45}\mathrm{In}_{5}$. We report the results of a comparative study of the magnetic microstructure of bulk $\mathrm{Ni}_{50}\mathrm{Mn}_{45}\mathrm{In}_{5}$ Heusler alloys using magnetometry, synchrotron x-ray diffraction, and magnetic small-angle neutron scattering (SANS). By combining unpolarized and spin-polarized SANS (POLARIS) we demonstrate that a number of important conclusions regarding the mesoscopic spin structure can be made. In particular, the analysis of the magnetic neutron data suggests that nanoprecipitates with an effective ferromagnetic component form in an antiferromagnetic matrix on field annealing at $700 \, \mathrm{K}$. These particles represent sources of perturbation, which seem to give rise to magnetically disordered regions in the vicinity of the particle-matrix interface. Analysis of the spin-flip SANS cross section via the computation of the correlation function yields a value of $\sim 55 \, \mathrm{nm}$ for the particle size and $\sim 20 \, \mathrm{nm}$ for the size of the spin-canted region.
△ Less
Submitted 11 March, 2019;
originally announced March 2019.
-
Mastering hysteresis in magnetocaloric materials
Authors:
Oliver Gutfleisch,
Tino Gottschall,
Maximilian Fries,
Dimitri Benke,
Iliya Radulov,
Konstantin P. Skokov,
Heiko Wende,
Markus Gruner,
Mehmet Acet,
Peter Entel,
Michael Farle
Abstract:
Hysteresis is more than just an interesting oddity, which occurs in materials with a first-order transition. It is a real obstacle on the path from existing lab-scale prototypes of magnetic refrigerators towards commercialization of this potentially disruptive cooling technology. Indeed, the reversibility of the magnetocaloric effect, being essential for magnetic heat pumps, strongly depends on th…
▽ More
Hysteresis is more than just an interesting oddity, which occurs in materials with a first-order transition. It is a real obstacle on the path from existing lab-scale prototypes of magnetic refrigerators towards commercialization of this potentially disruptive cooling technology. Indeed, the reversibility of the magnetocaloric effect, being essential for magnetic heat pumps, strongly depends on the width of the thermal hysteresis and therefore it is necessary to understand the mechanisms causing hysteresis and to find solutions how to minimize losses associated with thermal hysteresis in order to maximize the efficiency of magnetic cooling devices. In this work, we discuss fundamental aspects, which can contribute to thermal hysteresis and we are developing strategies for at least partially overcoming the hysteresis problem in some selected classes of magnetocaloric materials with large application potential. Doing so, we refer to the most relevant classes of magnetic refrigerants La-Fe-Si-, Heusler- and Fe2P-type compounds.
△ Less
Submitted 9 June, 2016; v1 submitted 28 April, 2016;
originally announced April 2016.
-
Residual stress induced stabilization of martensite phase and its effect on the magneto-structural transition in Mn rich Ni-Mn-In/Ga magnetic shape memory alloys
Authors:
Sanjay Singh,
Pallavi Kushwaha,
F. Sceibel,
Hanns-Peter Liermann,
S. R. Barman,
M. Acet,
C. Felser,
Dhananjai Pandey
Abstract:
The irreversibility of the martensite transition in magnetic shape memory alloys (MSMAs) with respect to external magnetic field is one of the biggest challenges that limits their application as giant caloric materials. This transition is a magneto-structural transition that is accompanied with a steep drop in magnetization (i.e., 'delta M') around the martensite start temperature (Ms) due to the…
▽ More
The irreversibility of the martensite transition in magnetic shape memory alloys (MSMAs) with respect to external magnetic field is one of the biggest challenges that limits their application as giant caloric materials. This transition is a magneto-structural transition that is accompanied with a steep drop in magnetization (i.e., 'delta M') around the martensite start temperature (Ms) due to the lower magnetization of the martensite phase. In this communication, we show that 'delta M' around Ms in Mn rich Ni-Mn based MSMAs gets suppressed by two orders of magnitude in crushed powders due to the stabilization of the martensite phase at temperatures well above the Ms and the austenite finish (Af) temperatures due to residual stresses. Analysis of the intensities and the FWHM of the x-ray powder diffraction patterns reveals stabilized martensite phase fractions as 97, 75 and 90% with corresponding residual microstrains as 5.4, 5.6 and 3% in crushed powders of the three different Mn rich Ni-Mn alloys, namely, Mn1.8Ni1.8In0.4, Mn1.75Ni1.25Ga and Mn1.9Ni1.1Ga, respectively. Even after annealing at 773 K, the residual stress stabilised martensite phase does not fully revert to the equilibrium cubic austenite phase as the magneto-structural transition is only partially restored with reduced value of 'delta M'. Our results have very significant bearing on application of such alloys as inverse magnetocaloric and barocaloric materials.
△ Less
Submitted 31 May, 2015;
originally announced June 2015.
-
Effect of composition on magnetocaloric properties of Mn$ _{3} $Ga$ _{(1-x)} $Sn$ _{x} $C
Authors:
E. T. Dias,
K. R. Priolkar,
O. Cakir,
M. Acet,
A. K. Nigam
Abstract:
A study investigating the effect of Sn substitution on the magnetocaloric properties of Mn$ _{3} $Ga$ _{(1-x)} $Sn$ _{x} $C compounds reveals that nature of the MCE has a strong dependence on the nature of the magnetic ordering. For small amounts of Sn ($ x\leq0.2 $) the MCE is of the inverse type wherein an increase in the applied field beyond 5T gives rise to a table like temperature dependence…
▽ More
A study investigating the effect of Sn substitution on the magnetocaloric properties of Mn$ _{3} $Ga$ _{(1-x)} $Sn$ _{x} $C compounds reveals that nature of the MCE has a strong dependence on the nature of the magnetic ordering. For small amounts of Sn ($ x\leq0.2 $) the MCE is of the inverse type wherein an increase in the applied field beyond 5T gives rise to a table like temperature dependence of the entropy due to a coupling between the first order FM - AFM transition and the field induced AFM - FM transition. Replacement of Ga by larger concentrations of Sn ($ x\geq0.71 $) $(ΔS_M)$ results in a change of the MCE to a conventional type with very little variation in the position of $(ΔS_M)_{max}$ with increasing magnetic field. This has been explained to be due to the local strain introduced by A site ions (Ga/Sn) which affect the magnetostructural coupling in these compounds.
△ Less
Submitted 14 March, 2015;
originally announced March 2015.
-
Effect of local structural distortions on magnetostructural transformation in Mn$_3$SnC
Authors:
E. T. Dias,
K. R. Priolkar,
A. Das,
G. Aquilanti,
Ö. Çakir,
M. Acet,
A. K. Nigam
Abstract:
In this paper we attempt to understand the different nature of first order magnetic transformation in Mn$_3$SnC as compared to that in Mn$_3$GaC. The transformation in Mn$_3$SnC is close to room temperature (T$_t \approx$ 280K) and is associated with a large change in magnetic entropy that makes it a suitable candidate for applications in ferroic cooling. Using a combination of x-ray and neutron d…
▽ More
In this paper we attempt to understand the different nature of first order magnetic transformation in Mn$_3$SnC as compared to that in Mn$_3$GaC. The transformation in Mn$_3$SnC is close to room temperature (T$_t \approx$ 280K) and is associated with a large change in magnetic entropy that makes it a suitable candidate for applications in ferroic cooling. Using a combination of x-ray and neutron diffraction and x-ray absorption fine structure (XAFS) spectroscopy we infer that the magnetic ground state consisting of antiferromagnetic and ferromagnetic Mn atoms is due to structural distortions present in Mn$_6$C octahedra.
△ Less
Submitted 16 February, 2015;
originally announced February 2015.
-
Phase formation characteristics and magnetic properties of bulk Ni2MnGe Heusler alloy
Authors:
U. Adem,
I. Dincer,
S. Akturk,
M. Acet,
Y. Elerman
Abstract:
We have systemically studied the effects of annealing temperature and alloy composition on the structural and magnetic properties of bulk Ni$_{2}$MnGe and Ni$_{2.1}$Mn$_{0.9}$Ge Heusler alloys. We have observed that both annealing temperature and the alloy composition drastically alter the phases found in the samples due to the presence of competing ternary phases. Annealing at 900 and 950…
▽ More
We have systemically studied the effects of annealing temperature and alloy composition on the structural and magnetic properties of bulk Ni$_{2}$MnGe and Ni$_{2.1}$Mn$_{0.9}$Ge Heusler alloys. We have observed that both annealing temperature and the alloy composition drastically alter the phases found in the samples due to the presence of competing ternary phases. Annealing at 900 and 950 $^{\circ}$C for both alloy compositions facilitate the formation of L2$_{1}$ Heusler phase. Nevertheless, formation of Ni$_{5}$Mn$_{4}$Ge$_{3}$ and Ni$_{16}$Mn$_{6}$Ge$_{7}$ phases cannot be prevented for Ni$_{2}$MnGe and Ni$_{2.1}$Mn$_{0.9}$Ge alloys, respectively. In order to estimate the magnetic contribution of the Ni$_{5}$Mn$_{4}$Ge$_{3}$ impurity phase to that of the parent Ni$_{2}$MnGe, we have also synthesized pure Ni$_{5}$Mn$_{4}$Ge$_{3}$ alloy. Antiferromagnetic nature of Ni$_{5}$Mn$_{4}$Ge$_{3}$ with low magnetization response allows us to reveal the magnetic response of the stoichiometric bulk Ni$_{2}$MnGe. Bulk Ni$_{2}$MnGe shows simple ferromagnetic behavior with a Curie temperature of 300 K, in agreement with the previous results on thin films. Despite the divergence of magnetization curves between field cooled (FC) and field heated (FH) modes, stoichiometric Ni$_{2}$MnGe alloy does not undergo a martensitic phase transition based on our variable temperature x-ray diffraction experiments.
△ Less
Submitted 19 August, 2014;
originally announced August 2014.
-
Advanced materials for solid-state refrigeration
Authors:
Lluis Manosa,
Antoni Planes,
Mehmet Acet
Abstract:
Recent progress on caloric effects are reviewed. The application of external stimuli such as magnetic field, hydrostatic pressure, uniaxial stress and electric field give rise respectively to magnetocaloric, barocaloric, elastocaloric and electrocaloric effects. The values of the relevant quantities such as isothermal entropy and adiabatic temperature-changes are compiled for selected materials. L…
▽ More
Recent progress on caloric effects are reviewed. The application of external stimuli such as magnetic field, hydrostatic pressure, uniaxial stress and electric field give rise respectively to magnetocaloric, barocaloric, elastocaloric and electrocaloric effects. The values of the relevant quantities such as isothermal entropy and adiabatic temperature-changes are compiled for selected materials. Large values for these quantities are found when the material is in the vicinity of a phase transition. Quite often there is coupling between different degrees of freedom, and the material can exhibit cross-response to different external fields. In this case, the material can exhibit either conventional or inverse caloric effects when a field is applied. The values reported for the many caloric effects at moderate fields are large enough to envisage future application of these materials in efficient and environmental friendly refrigeration.
△ Less
Submitted 15 March, 2013;
originally announced March 2013.
-
Lattice dynamics in magnetic superelastic Ni-Mn-In alloys. Neutron scattering and ultrasonic experiments
Authors:
Xavier Moya,
David Gonzalez-Alonso,
Lluis Manosa,
Antoni Planes,
V. O. Garlea,
T. A. Lograsso,
D. L. Schlagel,
J. L. Zarestky,
Seda Aksoy,
Mehmet Acet
Abstract:
Neutron scattering and ultrasonic methods have been used to study the lattice dynamics of two single crystals of Ni-Mn-In Heusler alloys close to Ni$_{50}$Mn$_{34}$In$_{16}$ magnetic superelastic composition. The paper reports the experimental determination of the low-lying phonon dispersion curves and the elastic constants for this alloy system. We found that the frequencies of the TA$_{2}$ bra…
▽ More
Neutron scattering and ultrasonic methods have been used to study the lattice dynamics of two single crystals of Ni-Mn-In Heusler alloys close to Ni$_{50}$Mn$_{34}$In$_{16}$ magnetic superelastic composition. The paper reports the experimental determination of the low-lying phonon dispersion curves and the elastic constants for this alloy system. We found that the frequencies of the TA$_{2}$ branch are relatively low and it exhibits a small dip anomaly at a wave number $ξ_{0} \approx 1/3$, which softens with decreasing temperature. Associated with the softening of this phonon, we also observed the softening of the shear elastic constant $C'=(C_{11}-C_{12})/2$. Both temperature softenings are typical for bcc based solids which undergo martensitic transformations and reflect the dynamical instability of the cubic lattice against shearing of $\{110\}$ planes along $<1\bar{1}0>$ directions. Additionally, we measured low-lying phonon dispersion branches and elastic constants in applied magnetic fields aimed to characterize the magnetoelastic coupling.
△ Less
Submitted 19 June, 2009;
originally announced June 2009.
-
Phase diagram of Fe-doped Ni-Mn-Ga ferromagnetic shape-memory alloys
Authors:
Daniel Soto,
Francisco Alvarado Hernandez,
Horacio Flores,
Xavier Moya,
Lluis Manosa,
Antoni Planes,
Seda Aksoy,
Mehmet Acet,
Thorsten Krenke
Abstract:
We have studied the effect of Fe addition on the structural and magnetic transitions in the magnetic shape memory alloy Ni-Mn-Ga by substituting systematically each atomic species by Fe. Calorimetric and AC susceptibility measurements have been carried out in order to study the magnetic and structural transformation properties. We find that the addition of Fe modifies the structural and magnetic…
▽ More
We have studied the effect of Fe addition on the structural and magnetic transitions in the magnetic shape memory alloy Ni-Mn-Ga by substituting systematically each atomic species by Fe. Calorimetric and AC susceptibility measurements have been carried out in order to study the magnetic and structural transformation properties. We find that the addition of Fe modifies the structural and magnetic transformation temperatures. Magnetic transition temperatures are displaced to higher values when Fe is substituted into Ni-Mn-Ga, while martensitic and premartensitic transformation temperatures shift to lower values. Moreover, it has been found that the electron per atom concentration essentially governs the phase stability in the quaternary system. However, the observed scaling of transition temperatures with $e/a$ differs from that reported in the related ternary system Ni-Mn-Ga.
△ Less
Submitted 8 April, 2008;
originally announced April 2008.
-
Effects of hydrostatic pressure on the magnetism and martensitic transition of Ni-Mn-In magnetic superelastic alloys
Authors:
Lluis Manosa,
Xavier Moya,
Antoni Planes,
Oliver Gutfleisch,
Julia Lyubina,
Maria Barrio,
Josep-Lluis Tamarit,
Seda Aksoy,
Thorsten Krenke,
Mehmet Acet
Abstract:
We report magnetization and differential thermal analysis measurements as a function of pressure accross the martensitic transition in magnetically superelastic Ni-Mn-In alloys. It is found that the properties of the martensitic transformation are significantly affected by the application of pressure. All transition temperatures shift to higher values with increasing pressure. The largest rate o…
▽ More
We report magnetization and differential thermal analysis measurements as a function of pressure accross the martensitic transition in magnetically superelastic Ni-Mn-In alloys. It is found that the properties of the martensitic transformation are significantly affected by the application of pressure. All transition temperatures shift to higher values with increasing pressure. The largest rate of temperature shift with pressure has been found for Ni$_{50}$Mn$_{34}$In$_{16}$ as a consequence of its small entropy change at the transition. Such a strong pressure dependence of the transition temperature opens up the possibility of inducing the martensitic transition by applying relatively low hydrostatic pressures.
△ Less
Submitted 21 December, 2007;
originally announced December 2007.
-
Tailoring magnetic and magnetocaloric properties of martensitic transitions in ferromagnetic Heusler alloys
Authors:
Seda Aksoy,
Thorsten Krenke,
Mehmet Acet,
Eberhard F. Wassermann,
Xavier Moya,
Lluis Manosa,
Antoni Planes
Abstract:
Ni$_{50}$Mn$_{34}$In$_{16}$ undergoes a martensitic transformation around 250 K and exhibits a field induced reverse martensitic transformation and substantial magnetocaloric effects. We substitute small amounts Ga for In, which are isoelectronic, to carry these technically important properties to close to room temperature by shifting the martensitic transformation temperature.
Ni$_{50}$Mn$_{34}$In$_{16}$ undergoes a martensitic transformation around 250 K and exhibits a field induced reverse martensitic transformation and substantial magnetocaloric effects. We substitute small amounts Ga for In, which are isoelectronic, to carry these technically important properties to close to room temperature by shifting the martensitic transformation temperature.
△ Less
Submitted 28 November, 2007;
originally announced November 2007.
-
Magnetization easy-axis in martensitic Heusler alloys estimated by strain measurements under magnetic-field
Authors:
Seda Aksoy,
Thorsten Krenke,
Mehmet Acet,
Eberhard F. Wassermann,
Xavier Moya,
Lluis Manosa,
Antoni Planes
Abstract:
We study the temperature dependence of strain under constant magnetic-fields in Ni-Mn based ferromagnetic Heusler alloys in the form Ni-Mn-$X$ ($X$: Ga, In, Sn, Sb) which undergo a martensitic transformation. We discuss the influence of the applied magnetic-field on the nucleation of ferromagnetic martensite and extract information on the easy-axis of magnetization in the martensitic state.
We study the temperature dependence of strain under constant magnetic-fields in Ni-Mn based ferromagnetic Heusler alloys in the form Ni-Mn-$X$ ($X$: Ga, In, Sn, Sb) which undergo a martensitic transformation. We discuss the influence of the applied magnetic-field on the nucleation of ferromagnetic martensite and extract information on the easy-axis of magnetization in the martensitic state.
△ Less
Submitted 5 November, 2007;
originally announced November 2007.
-
Effect of Co and Fe on the inverse magnetocaloric properties of Ni-Mn-Sn
Authors:
Thorsten Krenke,
Eyup Duman,
Mehmet Acet,
Xavier Moya,
Lluis Manosa,
Antoni Planes
Abstract:
At certain compositions Ni-Mn-$X$ Heusler alloys ($X$: group IIIA-VA elements) undergo martensitic transformations, and many of them exhibit inverse magnetocaloric effects. In alloys where $X$ is Sn, the isothermal entropy change is largest among the Heusler alloys, particularly in Ni$_{50}$Mn$_{37}$Sn$_{13}$ where it reaches a value of 20 Jkg$^{-1}$K$^{-1}$ for a field of 5T. We substitute Ni w…
▽ More
At certain compositions Ni-Mn-$X$ Heusler alloys ($X$: group IIIA-VA elements) undergo martensitic transformations, and many of them exhibit inverse magnetocaloric effects. In alloys where $X$ is Sn, the isothermal entropy change is largest among the Heusler alloys, particularly in Ni$_{50}$Mn$_{37}$Sn$_{13}$ where it reaches a value of 20 Jkg$^{-1}$K$^{-1}$ for a field of 5T. We substitute Ni with Fe and Co in this alloy, each in amounts of 1 at% and 3 at% to perturb the electronic concentration and examine the resulting changes in the magnetocaloric properties. Increasing both Fe and Co concentrations causes the martensitic transition temperature to decrease, whereby the substitution by Co at both compositions or substituting 1 at% Fe leads to a decrease in the magnetocaloric effect. On the other hand, the magnetocaloric effect in the alloy with 3 at% Fe leads to an increase in the value of the entropy change to about 30 Jkg$^{-1}$K$^{-1}$ at 5T.
△ Less
Submitted 3 July, 2007;
originally announced July 2007.
-
Magnetic superelasticity and inverse magnetocaloric effect in Ni-Mn-In
Authors:
Thorsten Krenke,
Eyup Duman,
Mehmet Acet,
Eberhard F. Wassermann,
Xavier Moya,
Lluis Manosa,
Antoni Planes,
Emmanuelle Suard,
Bachir Ouladdiaf
Abstract:
Applying a magnetic field to a ferromagnetic Ni$_{50}$Mn$_{34}$In$_{16}$ alloy in the martensitic state induces a structural phase transition to the austenitic state. This is accompanied by a strain which recovers on removing the magnetic field giving the system a magnetically superelastic character. A further property of this alloy is that it also shows the inverse magnetocaloric effect. The ma…
▽ More
Applying a magnetic field to a ferromagnetic Ni$_{50}$Mn$_{34}$In$_{16}$ alloy in the martensitic state induces a structural phase transition to the austenitic state. This is accompanied by a strain which recovers on removing the magnetic field giving the system a magnetically superelastic character. A further property of this alloy is that it also shows the inverse magnetocaloric effect. The magnetic superelasticity and the inverse magnetocaloric effect in Ni-Mn-In and their association with the first order structural transition is studied by magnetization, strain, and neutron diffraction studies under magnetic field.
△ Less
Submitted 10 April, 2007;
originally announced April 2007.
-
Cooling and heating by adiabatic magnetization in the Ni$_{50}$Mn$_{34}$In$_{16}$ magnetic shape memory alloy
Authors:
Xavier Moya,
Lluis Manosa,
Antoni Planes,
Seda Aksoy,
Mehmet Acet,
Eberhard F. Wassermann,
Thorsten Krenke
Abstract:
We report on measurements of the adiabatic temperature change in the inverse magnetocaloric Ni$_{50}$Mn$_{34}$In$_{16}$ alloy. It is shown that this alloy heats up with the application of a magnetic field around the Curie point due to the conventional magnetocaloric effect. In contrast, the inverse magnetocaloric effect associated with the martensitic transition results in the unusual decrease o…
▽ More
We report on measurements of the adiabatic temperature change in the inverse magnetocaloric Ni$_{50}$Mn$_{34}$In$_{16}$ alloy. It is shown that this alloy heats up with the application of a magnetic field around the Curie point due to the conventional magnetocaloric effect. In contrast, the inverse magnetocaloric effect associated with the martensitic transition results in the unusual decrease of temperature by adiabatic magnetization. We also provide magnetization and specific heat data which enable to compare the measured temperature changes to the values indirectly computed from thermodynamic relationships. Good agreement is obtained for the conventional effect at the second-order paramagnetic-ferromagnetic phase transition. However, at the first order structural transition the measured values at high fields are lower than the computed ones. Irreversible thermodynamics arguments are given to show that such a discrepancy is due to the irreversibility of the first-order martensitic transition.
△ Less
Submitted 10 April, 2007;
originally announced April 2007.
-
Temperature and magnetic field dependences of the elastic constants of Ni-Mn-Al magnetic Heusler alloys
Authors:
Xavier Moya,
Lluis Manosa,
Antoni Planes,
Thorsten Krenke,
Mehmet Acet,
Michel Morin,
J. L. Zarestky,
T. A. Lograsso
Abstract:
We report on measurements of the adiabatic second order elastic constants of the off-stoichiometric Ni$_{54}$Mn$_{23}$Al$_{23}$ single crystalline Heusler alloy. The variation in the temperature dependence of the elastic constants has been investigated across the magnetic transition and over a broad temperature range. Anomalies in the temperature behaviour of the elastic constants have been foun…
▽ More
We report on measurements of the adiabatic second order elastic constants of the off-stoichiometric Ni$_{54}$Mn$_{23}$Al$_{23}$ single crystalline Heusler alloy. The variation in the temperature dependence of the elastic constants has been investigated across the magnetic transition and over a broad temperature range. Anomalies in the temperature behaviour of the elastic constants have been found in the vicinity of the magnetic phase transition. Measurements under applied magnetic field, both isothermal and variable temperature, show that the value of the elastic constants depends on magnetic order, thus giving evidence for magnetoelastic coupling in this alloy system.
△ Less
Submitted 2 June, 2006;
originally announced June 2006.
-
Lattice dynamics and phonon softening in Ni-Mn-Al Heusler alloys
Authors:
Xavier Moya,
Lluís Mañosa,
Antoni Planes,
Thorsten Krenke,
Mehmet Acet,
V. O. Garlea,
T. A. Lograsso,
D. L. Schlagel,
J. L. Zarestky
Abstract:
Inelastic and elastic neutron scattering have been used to study a single crystal of the Ni$_{54}$Mn$_{23}$Al$_{23}$ Heusler alloy over a broad temperature range. The paper reports the first experimental determination of the low-lying phonon dispersion curves for this alloy system. We find that the frequencies of the TA$_2$ modes are relatively low. This branch exhibits an anomaly (dip) at a wav…
▽ More
Inelastic and elastic neutron scattering have been used to study a single crystal of the Ni$_{54}$Mn$_{23}$Al$_{23}$ Heusler alloy over a broad temperature range. The paper reports the first experimental determination of the low-lying phonon dispersion curves for this alloy system. We find that the frequencies of the TA$_2$ modes are relatively low. This branch exhibits an anomaly (dip) at a wave number $ξ_{0} ={1/3}\approx 0.33$, which softens with decreasing temperature. Associated with this anomalous dip at $ξ_{0}$, an elastic central peak scattering is also present. We have also observed satellites due to the magnetic ordering.
△ Less
Submitted 24 January, 2006;
originally announced January 2006.
-
Anomalous vibrational effects in non-magnetic and magnetic Heusler alloys
Authors:
A. T. Zayak,
P. Entel,
K. M. Rabe,
W. A. Adeagbo,
M. Acet
Abstract:
First-principles calculations are used in order to investigate phonon anomalies in non-magnetic and magnetic Heusler alloys. Phonon dispersions for several systems in their cubic L2$\mathrm{_1}$ structure were obtained along the [110] direction. We consider compounds which exhibit phonon instabilities and compare them with their stable counterparts. The analysis of the electronic structure allow…
▽ More
First-principles calculations are used in order to investigate phonon anomalies in non-magnetic and magnetic Heusler alloys. Phonon dispersions for several systems in their cubic L2$\mathrm{_1}$ structure were obtained along the [110] direction. We consider compounds which exhibit phonon instabilities and compare them with their stable counterparts. The analysis of the electronic structure allows us to identify the characteristic features leading to structural instabilities. The phonon dispersions of the unstable compounds show that, while the acoustic modes tend to soften, the optical modes disperse in a way which is significantly different from that of the stable structures. The optical modes that appear to disperse at anomalously low frequencies are Raman active, which is considered an indication of a stronger polarizability of the unstable systems. We show that phonon instability of the TA$_{2}$ mode in Heusler alloys is driven by interaction(repulsion) with the low energy optical vibrations. The optical modes show their unusual behavior due to covalent interactions which are additional bonding features incommensurate with the dominating metallicity in Heusler compounds.
△ Less
Submitted 29 June, 2005;
originally announced June 2005.
-
Inverse magnetocaloric effect in ferromagnetic Ni-Mn-Sn alloys
Authors:
Thorsten Krenke,
Eyup Duman,
Mehmet Acet,
Eberhard F. Wassermann,
Xavier Moya,
Lluis Manosa,
Antoni Planes
Abstract:
The magnetocaloric effect (MCE) in paramagnetic materials has been widely used for attaining very low temperatures by applying a magnetic field isothermally and removing it adiabatically. The effect can be exploited also for room temperature refrigeration by using recently discovered giant MCE materials. In this letter, we report on an inverse situation in Ni-Mn-Sn alloys, whereby applying a mag…
▽ More
The magnetocaloric effect (MCE) in paramagnetic materials has been widely used for attaining very low temperatures by applying a magnetic field isothermally and removing it adiabatically. The effect can be exploited also for room temperature refrigeration by using recently discovered giant MCE materials. In this letter, we report on an inverse situation in Ni-Mn-Sn alloys, whereby applying a magnetic field adiabatically, rather than removing it, causes the sample to cool. This has been known to occur in some intermetallic compounds, for which a moderate entropy increase can be induced when a field is applied, thus giving rise to an inverse magnetocaloric effect. However, the entropy change found for some ferromagnetic Ni-Mn-Sn alloys is just as large as that reported for giant MCE materials, but with opposite sign. The giant inverse MCE has its origin in a martensitic phase transformation that modifies the magnetic exchange interactions due to the change in the lattice parameters.
△ Less
Submitted 26 May, 2005;
originally announced May 2005.
-
Magnetovolume instabilities in the pressure dependence of the K-edge circular dichroism of Fe3C Invar particles
Authors:
E. Duman,
M. Acet,
E. F. Wassermann,
J. P. Itie,
F. Baudelet,
O. Mathon,
S. Pascarelli
Abstract:
The p-electrons of carbon in the interstitial compound Fe3C hybridize with the Fe d-band and enhance the valence electron concentration of Fe from 8 to 8.67. At this concentration, substitutional 3d transition metals and alloys exhibit strong moment-volume coupling phenomena and associated magnetovolume instabilities, otherwise known as the Invar effect. For this reason, Fe3C is also expected to…
▽ More
The p-electrons of carbon in the interstitial compound Fe3C hybridize with the Fe d-band and enhance the valence electron concentration of Fe from 8 to 8.67. At this concentration, substitutional 3d transition metals and alloys exhibit strong moment-volume coupling phenomena and associated magnetovolume instabilities, otherwise known as the Invar effect. For this reason, Fe3C is also expected to incorporate a strong magnetovolume instability, and therefore, we examine the pressure dependence of the of the K edge x-ray magnetic circular dichroism in Fe3C at ambient temperature and pressures up to 20 GPa. We and clear evidence for a high-moment to low-moment transition at about 10 GPa.
△ Less
Submitted 6 October, 2004;
originally announced October 2004.
-
Disorder induced critical phenomena in magnetically glassy Cu-Al-Mn alloys
Authors:
Jordi Marcos,
Eduard Vives,
Lluis Manosa,
Mehmet Acet,
Eyup Duman,
Michel Morin,
Vaclav Novak,
Antoni Planes
Abstract:
Measurements of magnetic hysteresis loops in Cu-Al-Mn alloys of different Mn content at low temperatures are presented. The loops are smooth and continuous above a certain temperature, but exhibit a magnetization discontinuity below that temperature. Scaling analysis suggest that this system displays a disorder induced phase transition line. Measurements allow to determine the critical exponents…
▽ More
Measurements of magnetic hysteresis loops in Cu-Al-Mn alloys of different Mn content at low temperatures are presented. The loops are smooth and continuous above a certain temperature, but exhibit a magnetization discontinuity below that temperature. Scaling analysis suggest that this system displays a disorder induced phase transition line. Measurements allow to determine the critical exponents $β=0.03\pm 0.01$ and $βδ= 0.4 \pm 0.1$ in agreement with those reported recently [Berger et al., Phys. Rev. Lett. {\bf 85}, 4176 (2000)]
△ Less
Submitted 13 September, 2002;
originally announced September 2002.