Structural Inhomogeneities and Suppressed Magneto-Structural Coupling in Mn-Substituted GeCo2O4
Authors:
Shivani Sharma,
Pooja Jain,
Benny Schundelmier,
Chin-Wei Wang,
Poonam Yadav,
Adrienn Maria Szucs,
Kaya Wei,
N. P. Lalla,
Theo Siegrist
Abstract:
A comprehensive study of Ge1-xMnxCo2O4 (GMCO) system was conducted using neutron powder diffraction (NPD), x-ray diffraction (XRD), Scanning electron microscopy, magnetometry, and heat capacity measurements. Comparative analysis with GeCo2O4 (GCO) highlights the influence of Mn substitution on the crystal and magnetic structure at low temperature. Surprisingly, phase separation is observed in GMCO…
▽ More
A comprehensive study of Ge1-xMnxCo2O4 (GMCO) system was conducted using neutron powder diffraction (NPD), x-ray diffraction (XRD), Scanning electron microscopy, magnetometry, and heat capacity measurements. Comparative analysis with GeCo2O4 (GCO) highlights the influence of Mn substitution on the crystal and magnetic structure at low temperature. Surprisingly, phase separation is observed in GMCO with a targeted nominal composition of Ge0.5Mn0.5Co2O4. SEM/EDX analysis reveals that the sample predominantly consists of a Mn-rich primary phase with approximate stoichiometry Mn0.74Ge0.18Co2O4, along with a minor Ge-rich secondary phase of composition Ge0.91Mn0.19Co2O4. Although both GCO and GMCO crystallize in cubic symmetry at room temperature, a substantial difference in low-temperature structural properties has been observed. Magnetic and heat capacity data indicate ferrimagnetic ordering in the Mn-rich phase near TC = 108 K, while the Ge-rich phase exhibits antiferromagnetic order at TN = 22 K in GMCO. Analysis of heat capacity data reveals that the estimated magnetic entropy amounts to only 63% of the theoretical value expected in GMCO. A collinear ferrimagnetic arrangement is observed in the Mn rich phase below the magnetic ordering temperature, characterized by antiparallel spins of the Mn at A site and Co at B site along the c-direction. At 5 K, the refined magnetic moments are 2.31(3) for MnA and 1.82(3) uB for CoB in the Mn rich ferrimagnetic phase. The magnetic structure at 5 K in the Ge rich secondary phase is identical to the antiferromagnetic structure of the parent compound GeCo2O4. The refined value of the CoB moment in this phase at 5 K is 2.53(3) uB.
△ Less
Submitted 16 June, 2025;
originally announced June 2025.
Structural and Magnetic properties of Ge0.5Mn0.5Co2O4 using neutron diffraction
Authors:
Pooja Jain,
Benny Schundelmier,
Chin-Wei Wang,
Poonam Yadav,
Kaya Wei,
N. P. Lalla,
Shivani Sharma
Abstract:
The structural and magnetic properties of Ge0.5Mn0.5Co2O4 (GMCO) have been investigated in detail utilizing neutron powder diffraction (NPD), x-ray diffraction (XRD), DC magnetometry, and heat capacity analysis and compared with GeCo2O4. Despite both compounds exhibiting a cubic structure at room temperature, a substantial difference on low temperature structural properties have been observed for…
▽ More
The structural and magnetic properties of Ge0.5Mn0.5Co2O4 (GMCO) have been investigated in detail utilizing neutron powder diffraction (NPD), x-ray diffraction (XRD), DC magnetometry, and heat capacity analysis and compared with GeCo2O4. Despite both compounds exhibiting a cubic structure at room temperature, a substantial difference on low temperature structural properties have been observed for GMCO, indicating the effect of Mn substitution on crystal structure. The magnetic and heat capacity data reveal a ferrimagnetic ordering around 108 K in GMCO. A minor secondary phase is confirmed which undergoes long range AFM ordering at further lower temperatures. This secondary phase remains undetected in XRD due to identical lattice parameters. Furthermore, the analysis of heat capacity data indicates a broadening of the high-temperature transition, attributing to the short-range correlation persisting up to higher temperatures. The estimated magnetic entropy amounts is 63% of the value expected for GMCO. The missing entropy is likely linked with the short-range magnetic correlations persisting well above the transition temperature. Cation distribution at the A and B sites has been estimated in GMCO using NPD. Magnetic structures are also confirmed in the main phase as well as in the secondary phase using NPD analysis. The high-temperature transition corresponds to the ferrimagnetic ordering of A and B site cations in the main phase. A collinear ferrimagnetic arrangement of A and B site spins aligned parallel to c axis is observed. The average values of A and B site moments in the ferrimagnetic phase at 5 K are 2.31(3) and 1.82(3)mB, respectively, with the temperature dependence of moments following the expected power law behavior. The low-temperature ordering is attributed to the antiferromagnetic ordering of B site ions associated with the secondary phase, something similar to GeCo2O4.
△ Less
Submitted 1 July, 2024;
originally announced July 2024.