Characterization of Three-Dimensional Microstructures in Single Crystal Diamond
Authors:
P. Olivero,
S. Rubanov,
P. Reichart,
B. C. Gibson,
S. T. Huntington,
J. R. Rabeau,
A. D. Greentree,
J. Salzman,
D. Moore,
D. N. Jamieson,
S. Prawer
Abstract:
We report on the Raman and photoluminescence characterization of three-dimensional microstructures created in single crystal diamond with a Focused Ion Beam (FIB) assisted lift-off technique. The method is based on MeV ion implantation to create a buried etchable layer, followed by FIB patterning and selective etching. In the applications of such microstructures where the properties of high qualit…
▽ More
We report on the Raman and photoluminescence characterization of three-dimensional microstructures created in single crystal diamond with a Focused Ion Beam (FIB) assisted lift-off technique. The method is based on MeV ion implantation to create a buried etchable layer, followed by FIB patterning and selective etching. In the applications of such microstructures where the properties of high quality single crystal diamond are most relevant, residual damage after the fabrication process represents a critical technological issue. The results of Raman and photoluminescence characterization indicate that the partial distortion of the sp3-bonded lattice and the formation of isolated point defects are effectively removed after thermal annealing, leaving low amounts of residual damage in the final structures. Three-dimensional microstructures in single-crystal diamond offer a large range of applications, such as quantum optics devices and fully integrated opto mechanical assemblies.
△ Less
Submitted 1 September, 2016;
originally announced September 2016.
-
Size-reduction of nanodiamonds via air oxidation
Authors:
T. Gaebel,
C. Bradac,
J. Chen,
P. Hemmer,
J. R. Rabeau
Abstract:
Here we report the size reduction and effects on nitrogen-vacancy centres in nanodiamonds by air oxidation using a combined atomic force and confocal microscope. The average height reduction of individual crystals as measured by atomic force microscopy was 10.6 nm/h at 600 °C air oxidation at atmospheric pressure. The oxidation process modified the surface including removal of non-diamond carbon a…
▽ More
Here we report the size reduction and effects on nitrogen-vacancy centres in nanodiamonds by air oxidation using a combined atomic force and confocal microscope. The average height reduction of individual crystals as measured by atomic force microscopy was 10.6 nm/h at 600 °C air oxidation at atmospheric pressure. The oxidation process modified the surface including removal of non-diamond carbon and organic material which also led to a decrease in background fluorescence. During the course of the nanodiamond size reduction, we observed the annihilation of nitrogen-vacancy centres which provided important insight into the formation of colour centres in small crystals. In these unirradiated samples, the smallest nanodiamond still hosting a stable nitrogen-vacancy centre observed was 8 nm.
△ Less
Submitted 27 April, 2011;
originally announced April 2011.
-
Enhanced spontaneous emission from nanodiamond colour centres on opal photonic crystal
Authors:
Faraz A Inam,
Torsten Gaebel,
Carlo Bradac,
Luke Stewart,
Michael J Withford,
Judith M Dawes,
James R Rabeau,
Michael J Steel
Abstract:
Colour centres in diamond are promising candidates as a platform for quantum technologies and biomedical imaging based on spins and/or photons. Controlling the emission properties of colour centres in diamond is a key requirement for developing efficient single photon sources with high collection efficiency. A number of groups have produced enhancement in the emission rate over narrow wavelength r…
▽ More
Colour centres in diamond are promising candidates as a platform for quantum technologies and biomedical imaging based on spins and/or photons. Controlling the emission properties of colour centres in diamond is a key requirement for developing efficient single photon sources with high collection efficiency. A number of groups have produced enhancement in the emission rate over narrow wavelength ranges by coupling single emitters in nanodiamond crystals to resonant electromagnetic structures. Here we characterise in detail the spontaneous emission rates of nitrogen-vacancy centres positioned in various locations on a structured substrate. We show an average factor of 1.5 enhancement of the total emission rate when nanodiamonds are on an opal photonic crystal surface, and observe changes in the lifetime distribution. We present a model to explain these observations and associate the lifetime properties with dipole orientation and polarization effects.
△ Less
Submitted 1 February, 2011; v1 submitted 31 January, 2011;
originally announced February 2011.
-
Coherence properties of a single dipole emitter in diamond
Authors:
Graham D. Marshall,
Torsten Gaebel,
Jonathan C. F. Matthews,
Jorg Enderlein,
Jeremy L. O'Brien,
James R. Rabeau
Abstract:
On-demand, high repetition rate sources of indistinguishable, polarised single photons are the key component for future photonic quantum technologies. Colour centres in diamond offer a promising solution, and the narrow line-width of the recently identified nickel-based NE8 centre makes it particularly appealing for realising the transform-limited sources necessary for quantum interference. Here w…
▽ More
On-demand, high repetition rate sources of indistinguishable, polarised single photons are the key component for future photonic quantum technologies. Colour centres in diamond offer a promising solution, and the narrow line-width of the recently identified nickel-based NE8 centre makes it particularly appealing for realising the transform-limited sources necessary for quantum interference. Here we report the characterisation of dipole orientation and coherence properties of a single NE8 colour centre in a diamond nanocrystal at room-temperature. We observe a single photon coherence time of 0.21 ps and an emission lifetime of 1.5 ns. Combined with an emission wavelength that is ideally suited for applications in existing quantum optical systems, these results show that the NE8 is a far more promising source than the more commonly studied nitrogen-vacancy centre and point the way to the realisation of a practical diamond colour centre-based single photon source.
△ Less
Submitted 12 September, 2010;
originally announced September 2010.
-
Prediction and measurement of the size-dependent stability of fluorescence in diamond over the entire nanoscale
Authors:
Carlo Bradac,
Torsten Gaebel,
Nishen Naidoo,
James R. Rabeau,
Amanda S. Barnard
Abstract:
Fluorescent defects in non-cytotoxic diamond nanoparticles are candidates for qubits in quantum computing, optical labels in biomedical imaging and sensors in magnetometry. For each application these defects need to be optically and thermodynamically stable, and included in individual particles at suitable concentrations (singly or in large numbers). In this letter, we combine simulations, theor…
▽ More
Fluorescent defects in non-cytotoxic diamond nanoparticles are candidates for qubits in quantum computing, optical labels in biomedical imaging and sensors in magnetometry. For each application these defects need to be optically and thermodynamically stable, and included in individual particles at suitable concentrations (singly or in large numbers). In this letter, we combine simulations, theory and experiment to provide the first comprehensive and generic prediction of the size, temperature and nitrogen-concentration dependent stability of optically active NV defects in nanodiamonds.
△ Less
Submitted 23 August, 2009;
originally announced August 2009.
-
Single nitrogen vacancy centers in chemical vapor deposited diamond nanocrystals
Authors:
J. R. Rabeau,
A. Stacey,
A. Rabeau,
F. Jelezko,
I. Mirza,
J. Wrachtrup,
S. Prawer
Abstract:
Nanodiamond crystals containing single color centers have been grown by chemical vapor deposition (CVD). The fluorescence from individual crystallites was directly correlated with crystallite size using a combined atomic force and scanning confocal fluorescence microscope. Under the conditions employed, the optimal size for single optically active nitrogen-vacancy (NV) center incorporation was m…
▽ More
Nanodiamond crystals containing single color centers have been grown by chemical vapor deposition (CVD). The fluorescence from individual crystallites was directly correlated with crystallite size using a combined atomic force and scanning confocal fluorescence microscope. Under the conditions employed, the optimal size for single optically active nitrogen-vacancy (NV) center incorporation was measured to be 60 to 70 nm. The findings highlight a strong dependence of NV incorporation on crystal size, particularly with crystals less than 50 nm in size.
△ Less
Submitted 25 September, 2007; v1 submitted 17 June, 2007;
originally announced June 2007.
-
Stark shift control of single optical centers in diamond
Authors:
Ph. Tamarat,
T. Gaebel,
J. R. Rabeau,
M. Khan,
A. D. Greentree,
H. Wilson,
L. C. L. Hollenberg,
S. Prawer,
P. Hemmer,
F. Jelezko,
J. Wrachtrup
Abstract:
Lifetime limited optical excitation lines of single nitrogen vacancy (NV) defect centers in diamond have been observed at liquid helium temperature. They display unprecedented spectral stability over many seconds and excitation cycles. Spectral tuning of the spin selective optical resonances was performed via the application of an external electric field (i.e. the Stark shift). A rich variety of…
▽ More
Lifetime limited optical excitation lines of single nitrogen vacancy (NV) defect centers in diamond have been observed at liquid helium temperature. They display unprecedented spectral stability over many seconds and excitation cycles. Spectral tuning of the spin selective optical resonances was performed via the application of an external electric field (i.e. the Stark shift). A rich variety of Stark shifts were observed including linear as well as quadratic components. The ability to tune the excitation lines of single NV centers has potential applications in quantum information processing.
△ Less
Submitted 25 July, 2006;
originally announced July 2006.
-
Room temperature coherent control of coupled single spins in solid
Authors:
T. Gaebel,
M. Domhan,
I. Popa,
C. Wittmann,
P. Neumann,
F. Jelezko,
J. R. Rabeau,
N. Stavrias,
A. D. Greentree,
S. Prawer,
J. Meijer,
J. Twamley,
P. R. Hemmer,
J. Wrachtrup
Abstract:
Coherent coupling between single quantum objects is at the heart of modern quantum physics. When coupling is strong enough to prevail over decoherence, it can be used for the engineering of correlated quantum states. Especially for solid-state systems, control of quantum correlations has attracted widespread attention because of applications in quantum computing. Such coherent coupling has been…
▽ More
Coherent coupling between single quantum objects is at the heart of modern quantum physics. When coupling is strong enough to prevail over decoherence, it can be used for the engineering of correlated quantum states. Especially for solid-state systems, control of quantum correlations has attracted widespread attention because of applications in quantum computing. Such coherent coupling has been demonstrated in a variety of systems at low temperature1, 2. Of all quantum systems, spins are potentially the most important, because they offer very long phase memories, sometimes even at room temperature. Although precise control of spins is well established in conventional magnetic resonance3, 4, existing techniques usually do not allow the readout of single spins because of limited sensitivity. In this paper, we explore dipolar magnetic coupling between two single defects in diamond (nitrogen-vacancy and nitrogen) using optical readout of the single nitrogen-vacancy spin states. Long phase memory combined with a defect separation of a few lattice spacings allow us to explore the strong magnetic coupling regime. As the two-defect system was well-isolated from other defects, the long phase memory times of the single spins was not diminished, despite the fact that dipolar interactions are usually seen as undesirable sources of decoherence. A coherent superposition of spin pair quantum states was achieved. The dipolar coupling was used to transfer spin polarisation from a nitrogen-vacancy centre spin to a nitrogen spin, with optical pumping of a nitrogen-vacancy centre leading to efficient initialisation. At the level anticrossing efficient nuclear spin polarisation was achieved. Our results demonstrate an important step towards controlled spin coupling and multi-particle entanglement in the solid state.
△ Less
Submitted 3 May, 2006;
originally announced May 2006.
-
Coherent Population Trapping in Diamond N-V Centers at Zero Magnetic Field
Authors:
Charles Santori,
David Fattal,
Sean M. Spillane,
Marco Fiorentino,
Raymond G. Beausoleil,
Andrew D. Greentree,
Paolo Olivero,
Martin Draganski,
James R. Rabeau,
Patrick Reichart,
Brant C. Gibson,
Sergey Rubanov,
David N. Jamieson,
Steven Prawer
Abstract:
Coherent population trapping at zero magnetic field was observed for nitrogen-vacancy centers in diamond under optical excitation. This was measured as a reduction in photoluminescence when the detuning between two excitation lasers matched the 2.88 GHz crystal-field splitting of the color center ground states. This behavior is highly sensitive to strain, which modifies the excited states, and w…
▽ More
Coherent population trapping at zero magnetic field was observed for nitrogen-vacancy centers in diamond under optical excitation. This was measured as a reduction in photoluminescence when the detuning between two excitation lasers matched the 2.88 GHz crystal-field splitting of the color center ground states. This behavior is highly sensitive to strain, which modifies the excited states, and was unexpected following recent experiments demonstrating optical readout of single nitrogen-vacancy electron spins based on cycling transitions. These results demonstrate for the first time that three-level Lambda configurations suitable for proposed quantum information applications can be realized simultaneously for all four orientations of nitrogen-vacancy centers at zero magnetic field.
△ Less
Submitted 31 May, 2006; v1 submitted 23 February, 2006;
originally announced February 2006.
-
Diamond chemical vapor deposition on optical fibers for fluorescence waveguiding
Authors:
J. R. Rabeau,
S. T. Huntington,
A. D. Greentree,
S. Prawer
Abstract:
A technique has been developed for depositing diamond crystals on the endfaces of optical fibers and capturing the fluorescence generated by optically active defects in the diamond into the fiber. This letter details the diamond growth on optical fibers and transmission of fluorescence through the fiber from the nitrogen-vacancy (N-V) color center in diamond. Control of the concentration of defe…
▽ More
A technique has been developed for depositing diamond crystals on the endfaces of optical fibers and capturing the fluorescence generated by optically active defects in the diamond into the fiber. This letter details the diamond growth on optical fibers and transmission of fluorescence through the fiber from the nitrogen-vacancy (N-V) color center in diamond. Control of the concentration of defects incorporated during the chemical vapor deposition (CVD) growth process is also demonstrated. These are the first critical steps in developing a fiber coupled single photon source based on optically active defect centers in diamond.
△ Less
Submitted 10 November, 2004;
originally announced November 2004.
-
Fabrication of single nickel-nitrogen defects in diamond by chemical vapor deposition
Authors:
J. R. Rabeau,
Y. L. Chin,
S. Prawer,
F. Jelezko,
T. Gaebel,
J. Wrachtrup
Abstract:
Fabrication of single nickel-nitrogen (NE8) defect centers in diamond by chemical vapor deposition is demonstrated. Under continuous-wave 745 nm laser excitation single defects were induced to emit single photon pulses at 797 nm with a linewidth of 1.5 nm at room temperature. Photon antibunching of single centers was demonstrated using a Hanbury-Brown and Twiss interferometer. Confocal images re…
▽ More
Fabrication of single nickel-nitrogen (NE8) defect centers in diamond by chemical vapor deposition is demonstrated. Under continuous-wave 745 nm laser excitation single defects were induced to emit single photon pulses at 797 nm with a linewidth of 1.5 nm at room temperature. Photon antibunching of single centers was demonstrated using a Hanbury-Brown and Twiss interferometer. Confocal images revealed approximately 10^6 optically active sites/cm^2 in the synthesized films. The fabrication of an NE8 based single photon source in synthetic diamond is important for fiber based quantum cryptography. It can also be used as an ideal point-like source for near-field optical microscopy.
△ Less
Submitted 9 November, 2004;
originally announced November 2004.
-
The role of C2 in nanocrystalline diamond growth
Authors:
J. R. Rabeau,
Y. Fan,
P. John,
J. I. B. Wilson
Abstract:
This paper presents findings from a study of nanocrystalline diamond (NCD) growth in a microwave plasma chemical vapour deposition (CVD) reactor. NCD films were grown using Ar/H2/CH4 and He/H2/CH4 gas compositions. The resulting films were characterised using Raman spectroscopy, scanning electron microscopy and atomic force microscopy. Analysis revealed an estimated grain size of the order of 50…
▽ More
This paper presents findings from a study of nanocrystalline diamond (NCD) growth in a microwave plasma chemical vapour deposition (CVD) reactor. NCD films were grown using Ar/H2/CH4 and He/H2/CH4 gas compositions. The resulting films were characterised using Raman spectroscopy, scanning electron microscopy and atomic force microscopy. Analysis revealed an estimated grain size of the order of 50 nm, growth rates in the range 0.01 to 0.3 um/h and sp3 and sp2 bonded carbon content consistent with that expected for NCD. The C2 Swan band was probed using cavity ring-down spectroscopy (CRDS) to measure the absolute C2 (a) number density in the plasma during diamond film growth. The number density in the Ar/H2/CH4 plasmas was in the range 2 to 4 x 10^12 cm-3, but found to be present in quantities too low to measure in the He/H2/CH4 plasmas. Optical emission spectrometry (OES) was employed to determine the relative densities of the C2 excited state (d) in the plasma. The fact that similar NCD material was grown whether using Ar or He as the carrier gas suggests that C2 does not play a major role in the growth of nanocrystalline diamond.
△ Less
Submitted 9 August, 2004;
originally announced August 2004.