Lithium plating induced degradation during fast charging of batteries subjected to compressive loading
Authors:
Prashant P. Gargh,
Abhishek Sarkar,
Ikenna C. Nlebedim,
Pranav Shrotriya
Abstract:
We report the lithium plating associated capacity loss during fast charging of compressively loaded lithium-ion batteries (LIBs). The charging and discharging of LIB under compressive loading during service may affect the cell performance or initiate localized defects in the electrodes. Pouch cells of capacity 20mAh were compressively loaded to nominal pressures of 0-440 kPa and subjected to 10 cy…
▽ More
We report the lithium plating associated capacity loss during fast charging of compressively loaded lithium-ion batteries (LIBs). The charging and discharging of LIB under compressive loading during service may affect the cell performance or initiate localized defects in the electrodes. Pouch cells of capacity 20mAh were compressively loaded to nominal pressures of 0-440 kPa and subjected to 10 cycles of fast charging at 1C and 4C. Experimental results show that cells charged at 4C-rate experienced significant capacity fade, and applying compressive loads exacerbated the capacity loss. The coulombic efficiency study shows that active lithium loss was higher for the initial cycles before gradually reducing to a minimal capacity loss for the tenth charging cycle. The cell voltage relaxation immediately after charging was monitored to identify the stripping of plated lithium after fast charging cycles and showed that the duration of lithium stripping was higher for cells under mechanical compressive loading. Scanning electron microscopy (SEM) and Electron paramagnetic resonance spectroscopy (EPR) characterization of the anode showed significantly higher lithium deposits on the anodes charged at a 4C rate under compressive loads. These results indicate that applied mechanical compression causes increased lithium plating during fast charging of batteries.
△ Less
Submitted 26 September, 2023;
originally announced September 2023.
-
Room Temperature Magnetocaloric Effect In CrTe1-XSex Alloys
Authors:
Morad Kh. Hamad,
I. C. Nlebedim,
Yazan Maswadec,
R. Hamad,
Kh. A. Ziq
Abstract:
Polycrystalline CrTe1-xSex samples were prepared using the conventional solid-state reaction technique and characterized by x-rad diffraction, temperature- and field- dependent magnetization for possible use in magnetocaloric cooling. Rietveld refinement revealed two phases in all prepared samples; a minor monoclinic phase that decreases with Se concentration until it vanishes near 10% of Se, and…
▽ More
Polycrystalline CrTe1-xSex samples were prepared using the conventional solid-state reaction technique and characterized by x-rad diffraction, temperature- and field- dependent magnetization for possible use in magnetocaloric cooling. Rietveld refinement revealed two phases in all prepared samples; a minor monoclinic phase that decreases with Se concentration until it vanishes near 10% of Se, and a major hexagonal one. At high temperature, CrTe1-xSex is paramagnetic, with ferromagnetic phase transition occurs at Tc ~332, 320, 318, 310, 299, and 295 K for x= 0.00, 0.02, 0.04, 0.06, 0.08, and 0.10, respectively. The magnetocaloric effect analysis (at H=5T) revealed a maximum magnetic entropy change of about 8.3, 7.9, 8.2, 9.1, 9.2, and 8.5 (J/kg.K) with a relative cooling power (RCP) value of about 555, 568, 547, 638, 694, and 668 (J/kg) around Tc for x= 0.00, 0.02, 0.04, 0.06, 0.08, and 0.10, respectively. Critical behavior analysis showed that the magnetic isotherms measured near Tc follow 3D Mean field critical exponents and a second order phase transition. A rigorous iteration estimated the critical exponents based on modified Arrott and Kouvel-fisher plots analysis, giving $β$ ~ 0.44, 0.51, 0.46, 0.49, 0.42, 0.49 and $γ$ ~ 1.02, 1.00, 0.99, 1.08, 1.07, 0.96, and 1.01 for x= 0.00, 0.02, 0.04, 0.06, 0.08, and 0.10, respectively.
△ Less
Submitted 13 November, 2022; v1 submitted 11 February, 2022;
originally announced February 2022.
-
Pressure dependent magnetic properties on bulk CrBr3 single crystals
Authors:
Rubyann Olmos,
Shamsul Alam,
Po Hao Chang,
Kinjal Gandha,
Ikenna C. Nlebedim,
Andrew Cole,
Fazel Tafti,
Rajendra Zope,
Srinivasa R. Singamaneni
Abstract:
The van der Waals class of materials offer an approach to two-dimensional magnetism as their spin fluctuations can be tuned upon exfoliation of layers. Moreover, it has recently been shown that spin-lattice coupling and long-range magnetic ordering can be modified with pressure in van der Waals materials. In this work, the magnetic properties of quasi two-dimensional CrBr3 are reported applying hy…
▽ More
The van der Waals class of materials offer an approach to two-dimensional magnetism as their spin fluctuations can be tuned upon exfoliation of layers. Moreover, it has recently been shown that spin-lattice coupling and long-range magnetic ordering can be modified with pressure in van der Waals materials. In this work, the magnetic properties of quasi two-dimensional CrBr3 are reported applying hydrostatic pressure. The application of pressure (0 - 0.8 GPa) shows a 72 % decrease in saturation magnetization with small decrease in the Curie temperature from 33 to 29 K. Density functional theory calculations with pressure up to 1 GPa show a reduction in volume and interplanar distance as pressure increases. To further understand magnetic properties with applied pressure, the magnetocrystalline anisotropy energy (MAE) and exchange coupling parameter (J) are calculated. There is minimal decrease in MAE and the first nearest neighbor interaction (J1) (U = 2.7 eV and J = 0.7 eV), shows an increase in J1 with respect to pressure. Overall, CrBr3 displays ferromagnetic interlayer coupling and the calculated exchange coupling and MAE parameters match well with the observations from the experimental work.
△ Less
Submitted 30 November, 2021;
originally announced December 2021.
-
Reinvestigation of the intrinsic magnetic properties of (Fe$_{1-x}$Co$_x$)$_2$B alloys and crystallization behavior of ribbons
Authors:
Tej Nath Lamichhane,
Olena Palasyuk,
Vladimir P. Antropov,
Ivan A. Zhuravlev,
Kirill D. Belashchenko,
Ikenna C. Nlebedim,
Kevin W. Dennis,
Anton Jesche,
Matthew J. Kramer,
Sergey L. Bud'ko,
R. William McCallum,
Paul C. Canfield,
Valentin Taufour
Abstract:
New determination of the magnetic anisotropy from single crystals of (Fe$_{1-x}$Co$_x$)$_2$B alloys are presented. The anomalous temperature dependence of the anisotropy constant is discussed using the standard Callen-Callen theory, which is shown to be insufficient to explain the experimental results. A more material specific study using first-principles calculations with disordered moments appro…
▽ More
New determination of the magnetic anisotropy from single crystals of (Fe$_{1-x}$Co$_x$)$_2$B alloys are presented. The anomalous temperature dependence of the anisotropy constant is discussed using the standard Callen-Callen theory, which is shown to be insufficient to explain the experimental results. A more material specific study using first-principles calculations with disordered moments approach gives a much more consistent interpretation of the experimental data. Since the intrinsic properties of the alloys with $x=0.3-0.35$ are promising for permanent magnets applications, initial investigation of the extrinsic properties are described, in particular the crystallization of melt spun ribbons with Cu, Al, and Ti additions. Previous attempts at developing a significant hysteresis have been unsuccessful in this system. Our melt-spinning experiment indicates that this system shows rapid crystallization.
△ Less
Submitted 29 July, 2020;
originally announced July 2020.
-
Fabrication of highly dense isotropic Nd-Fe-B bonded magnets via extrusion-based additive manufacturing
Authors:
Ling Li,
Kodey Jones,
Brian Sales,
Jason L. Pries,
I. C. Nlebedim,
Ke Jin,
Hongbin Bei,
Brian Post,
Michael Kesler,
Orlando Rios,
Vlastimil Kunc,
Robert Fredette,
John Ormerod,
Aaron Williams,
Thomas A. Lograsso,
M. Parans Paranthaman
Abstract:
Isotropic bonded magnets with a high loading fraction of 70 vol.% Nd-Fe-B are fabricated via an extrusion-based additive manufacturing, or 3D printing system that enables rapid production of large parts for the first time. The density of the printed magnet is 5.15 g/cm3. The room temperature magnetic properties are: intrinsic coercivity Hci = 8.9 kOe (708.2 kA/m), remanence Br = 5.8 kG (0.58 Tesla…
▽ More
Isotropic bonded magnets with a high loading fraction of 70 vol.% Nd-Fe-B are fabricated via an extrusion-based additive manufacturing, or 3D printing system that enables rapid production of large parts for the first time. The density of the printed magnet is 5.15 g/cm3. The room temperature magnetic properties are: intrinsic coercivity Hci = 8.9 kOe (708.2 kA/m), remanence Br = 5.8 kG (0.58 Tesla), and energy product (BH)max = 7.3 MGOe (58.1 kJ/m3). The as-printed magnets are then coated with two types of polymers, both of which improve the thermal stability at 127 °C as revealed by flux aging loss measurements. Tensile tests performed at 25 °C and 100 °C show that the ultimate tensile stress (UTS) increases with increasing loading fraction of the magnet powder, and decreases with increasing temperature. AC magnetic susceptibility and resistivity measurements show that the 3D printed Nd-Fe-B bonded magnets exhibit extremely low eddy current loss and high resistivity. Finally, we show that through back electromotive force measurements that motors installed with 3D printed Nd-Fe-B magnets exhibit similar performance as compared to those installed with sintered ferrites.
△ Less
Submitted 23 June, 2017;
originally announced June 2017.