A visco-plastic constitutive model for accurate densification and shape predictions in powder metallurgy hot isostatic pressing
Authors:
Subrato Sarkar,
Jason R Mayeur,
KPK Ajjarapu,
Fred A List III,
Soumya Nag,
Ryan R Dehoff
Abstract:
Powder metallurgy hot isostatic pressing (PM-HIP) is an advanced manufacturing process that produces near net shape parts with high material utilization and uniform microstructures. Despite being used frequently to produce small-scale components, the application of PM-HIP to large-scale components is limited due to inadequate understanding of its complex mechanisms that cause unpredictable post-HI…
▽ More
Powder metallurgy hot isostatic pressing (PM-HIP) is an advanced manufacturing process that produces near net shape parts with high material utilization and uniform microstructures. Despite being used frequently to produce small-scale components, the application of PM-HIP to large-scale components is limited due to inadequate understanding of its complex mechanisms that cause unpredictable post-HIP shape distortions. A computational model can provide necessary information about the intermediate and final stages of the HIP process that can help understand it better and make accurate predictions. Generally, two types of computational models are employed for PM-HIP simulations, namely, plastic and visco-plastic models. Between these, the plastic model is preferred due to its cheaper calibration approach requiring less experimental data. However, the plastic model sometimes produces incorrect predictions when slight variations of the HIP conditions are encountered in practical situations. Therefore, this work presents a visco-plastic model that addresses these limitations of the plastic model. A novel modified calibration approach is employed for the visco-plastic model that utilizes less experimental data than existing approaches. With the new approach, the data requirement is same for both plastic and visco-plastic models. This also enables a quantitative comparison of plastic and visco-plastic models, which have been only qualitatively compared in the past. When calibrated with the same experimental data, both the models are found to produce similar results. The calibrated visco-plastic model is applied to several complex geometries, and the predictions are found to be in good agreement with experimental observations.
△ Less
Submitted 13 June, 2025;
originally announced June 2025.
On narrowing coated conductor film: emergence of granularity-induced field hysteresis of transport critical current
Authors:
A. A. Gapud,
D. K. Christen,
R. Feenstra,
F. A. List III,
A. Khan
Abstract:
Critical current density Jc in polycrystalline or granular superconducting material is known to be hysteretic with applied field H due to the focusing of field within the boundary between adjacent grains. This is of concern in the so-called coated conductors wherein superconducting film is grown on a granular, but textured surface of a metal substrate. While previous work has mainly been on Jc d…
▽ More
Critical current density Jc in polycrystalline or granular superconducting material is known to be hysteretic with applied field H due to the focusing of field within the boundary between adjacent grains. This is of concern in the so-called coated conductors wherein superconducting film is grown on a granular, but textured surface of a metal substrate. While previous work has mainly been on Jc determined using induced or magnetization currents, the present work utilizes transport current via an applied potential in strip geometry. It is observed that the effect is not as pronounced using transport current, probably due to a large difference in criterion voltage between the two types of measurements. However, when the films are narrowed by patterning into 200-, 100-, or 80-micron, the hysteresis is clearly seen, because of the forcing of percolation across higher-angle grain boundaries. This effect is compared for films grown on ion-beam-assisted-deposited (IBAD) YSZ substrate and those grown on rolling-assisted-biaxially-textures substrates (RABiTS) which have grains that are about ten times larger. The hysteresis is more pronounced for the latter, which is more likely to have a weak grain boundary spanning the width of the microbridge. This is also of concern to applications in which coated conductors will be striated in order to reduce of AC losses.
△ Less
Submitted 9 January, 2008; v1 submitted 7 January, 2008;
originally announced January 2008.