Toward the theoretically observable limit of electron density distribution by single-crystal synchrotron X-ray diffraction: The case of orbitally ordered Ti-3d^1 in YTiO_3
Authors:
Terutoshi Sakakura,
Yoshihisa Ishikawa,
Shunji Kishimoto,
Yasuyuki Takenaka,
Kiyoaki Tanaka,
Shigeki Miyasaka,
Yoshinori Tokura,
Yukio Noda,
Nobuo Ishizawa,
Hajime Sagayama,
Hajime Yamamoto,
Hiroyuki Kimura
Abstract:
The theoretically observable limit of electron density distribution by single-crystal X-ray diffraction is discussed. When F_{orb} and δF are defined as, respectively, the partial structure factor for an orbital and the deviation of the observed F from the true F, the accuracy of electron density attributable to F_{orb} is chiefly determined by the number of reflections satisfying the condition F_…
▽ More
The theoretically observable limit of electron density distribution by single-crystal X-ray diffraction is discussed. When F_{orb} and δF are defined as, respectively, the partial structure factor for an orbital and the deviation of the observed F from the true F, the accuracy of electron density attributable to F_{orb} is chiefly determined by the number of reflections satisfying the condition F_{orb}/F > δF/F. Since F_{orb}/F, which is generally small for crystals with large F(0,0,0), is constant under a given set of experimental conditions, δF/F must be reduced to increase the number of reflections satisfying F_{orb}/F > δF/F. The present paper demonstrates how to reduce δF mathematically and experimentally, and the following topics are covered: the Poisson statistics, accumulation of errors in the data collection and reduction procedure, multiple diffraction, conversion error from F^2 to F in refinement programs, which is unavoidable when the input quantities have different dimension from F, weighting of reflections, and tips. For demonstration, observation of the electron density of the Ti-3d^1 orbital in YTiO_3 by synchrotron single-crystal X-ray diffraction is presented.
△ Less
Submitted 8 July, 2024; v1 submitted 31 December, 2023;
originally announced January 2024.
Origin of the Higher-$T_\rm{c}$ Phase in the K$_x$Fe$_{2-y}$Se$_2$ System
Authors:
Masashi Tanaka,
Yusuke Yanagisawa,
Masaya Fujioka,
Saleem J. Denholme,
Shiro Funahashi,
Yoshitaka Matsushita,
Nobuo Ishizawa,
Takahide Yamaguchi,
Hiroyuki Takeya,
Yoshihiko Takano
Abstract:
Single crystals of K$_x$Fe$_{2-y}$Se$_2$ are prepared by quenching at various temperatures. The crystals obtained at higher quenching temperatures have a surface morphology with mesh-like texture. They show a sharp superconducting transition at $T_\rm{c}$ ~32 K with a large shielding volume fraction. On the other hand, the crystals prepared without quenching show an onset superconducting transitio…
▽ More
Single crystals of K$_x$Fe$_{2-y}$Se$_2$ are prepared by quenching at various temperatures. The crystals obtained at higher quenching temperatures have a surface morphology with mesh-like texture. They show a sharp superconducting transition at $T_\rm{c}$ ~32 K with a large shielding volume fraction. On the other hand, the crystals prepared without quenching show an onset superconducting transition at ~44 K and a zero resistivity around ~33 K, and they possess island-like regions on the surface with a larger amount of Fe incorporation. In-situ high-temperature single crystal X-ray diffraction measurements tell us the Fe-vacancy ordered phase is generated at a temperature region around 270 °C via iron diffusion. The creation of this Fe-vacancy ordered phase may become a driving force of the growth of the higher $T_\rm{c}$ phase. The superconductivity at ~44 K is attributed to a metallic phase with no Fe-vacancy.
△ Less
Submitted 25 February, 2016; v1 submitted 16 April, 2015;
originally announced April 2015.