A computational framework to predict weld integrity and microstructural heterogeneity: application to hydrogen transmission
Authors:
J. Wijnen,
J. Parker,
M. Gagliano,
E. Martínez-Pañeda
Abstract:
We present a novel computational framework to assess the structural integrity of welds. In the first stage of the simulation framework, local fractions of microstructural constituents within weld regions are predicted based on steel composition and welding parameters. The resulting phase fraction maps are used to define heterogeneous properties that are subsequently employed in structural integrit…
▽ More
We present a novel computational framework to assess the structural integrity of welds. In the first stage of the simulation framework, local fractions of microstructural constituents within weld regions are predicted based on steel composition and welding parameters. The resulting phase fraction maps are used to define heterogeneous properties that are subsequently employed in structural integrity assessments using an elastoplastic phase field fracture model. The framework is particularised to predicting failure in hydrogen pipelines, demonstrating its potential to assess the feasibility of repurposing existing pipeline infrastructure to transport hydrogen. First, the process model is validated against experimental microhardness maps for vintage and modern pipeline welds. Additionally, the influence of welding conditions on hardness and residual stresses is investigated, demonstrating that variations in heat input, filler material composition, and weld bead order can significantly affect the properties within the weld region. Coupled hydrogen diffusion-fracture simulations are then conducted to determine the critical pressure at which hydrogen transport pipelines will fail. To this end, the model is enriched with a microstructure-sensitive description of hydrogen transport and hydrogen-dependent fracture resistance. The analysis of an X52 pipeline reveals that even 2 mm defects in a hard heat-affected zone can drastically reduce the critical failure pressure.
△ Less
Submitted 11 December, 2024;
originally announced December 2024.
Computational predictions of weld structural integrity in hydrogen transport pipelines
Authors:
T. K. Mandal,
J. Parker,
M. Gagliano,
E. Martínez-Pañeda
Abstract:
We combine welding process modelling with deformation-diffusion-fracture (embrittlement) simulations to predict failures in hydrogen transport pipelines. The focus is on the structural integrity of seam welds, as these are often the locations most susceptible to damage in gas transport infrastructure. Finite element analyses are conducted to showcase the ability of the model to predict cracking in…
▽ More
We combine welding process modelling with deformation-diffusion-fracture (embrittlement) simulations to predict failures in hydrogen transport pipelines. The focus is on the structural integrity of seam welds, as these are often the locations most susceptible to damage in gas transport infrastructure. Finite element analyses are conducted to showcase the ability of the model to predict cracking in pipeline steels exposed to hydrogen-containing environments. The validated model is then employed to quantify critical H$_2$ fracture pressures. The coupled, phase field-based simulations conducted provide insight into the role of existing defects, microstructural heterogeneity, and residual stresses. We find that under a combination of deleterious yet realistic conditions, the critical pressure at which fracture takes place can be as low as 15 MPa. These results bring new mechanistic insight into the viability of using the existing natural gas pipeline network to transport hydrogen, and the computational framework presented enables mapping the conditions under which this can be achieved safely.
△ Less
Submitted 21 January, 2024;
originally announced January 2024.