Graded composition Cd$_x$Zn$_{1-x}$Te films grown by Isothermal Close Space Sublimation technique
Authors:
O. de Melo,
A. Domínguez,
K. Gutiérrez Z-B,
G. Contreras-Puente,
S. Gallardo-Hernández,
A. Escobosa,
J. C. González,
R. Paniago,
J. Ferraz Dias,
M. Behar
Abstract:
Graded composition CdxZn1-xTe films were prepared by growing several alternate layers of CdTe and ZnTe by the Isothermal Close Space Sublimation technique. The thickness of both kinds of layers was modified along the structure to produce an increase of the average concentration of CdTe towards the surface of the films. Due to Zn/Cd inter-diffusion during the growth process the sequence of layers w…
▽ More
Graded composition CdxZn1-xTe films were prepared by growing several alternate layers of CdTe and ZnTe by the Isothermal Close Space Sublimation technique. The thickness of both kinds of layers was modified along the structure to produce an increase of the average concentration of CdTe towards the surface of the films. Due to Zn/Cd inter-diffusion during the growth process the sequence of layers was converted into a relatively smooth graded composition film. According to X- ray diffraction characterization the layers grew coherently with the (100) oriented GaAs substrates although they showed a relatively high mosaicity. Theta-2theta plots show very wide diffraction peaks as expected from variable composition samples. The band gap grading effect in light absorption was also verified through transmission measurements, using transparent substrates. Graded composition profiles of the thin films were confirmed by x-ray photoelectron and secondary ion mass spectroscopies. Moreover, quantitative Cd, Zn and Te profiles were obtained by the analysis of Rutherford backscattering spectra of the samples. This analysis showed a CdTe molar fraction profile ranging from approximately x = 0.8 at the surface of the sample and x = 0.35 at the interface with the substrate. The possibility of growing graded composition layers using a simple and cost-effective procedure was demonstrated. This could be interesting in technological applications like CdxZn1-xTe layers of variable composition in CdS/CdTe solar cells
△ Less
Submitted 17 September, 2019;
originally announced September 2019.
Processing and study of the composite CdS/Bi-Pb-Sr-Ca-Cu-O
Authors:
E. Díaz-Valdés,
G. S. Contreras-Puente,
N. Campos-Rivera,
C. Falcony-Guajardo,
R. Baquero
Abstract:
We have fabricated and characterized samples of the superconducting- semiconducting Bi-Pb-Sb-Sr-Ca-Cu-O/CdS composite. Nano-size particles of CdS were deposited and introduced into the porosities of the Bi-Pb-Sb-Sr-Ca-Cu-O material by the spray pyrolysis technique. The morphology and hollow size in the porous superconducting material as well as the grain size in CdS and the morphology of the surfa…
▽ More
We have fabricated and characterized samples of the superconducting- semiconducting Bi-Pb-Sb-Sr-Ca-Cu-O/CdS composite. Nano-size particles of CdS were deposited and introduced into the porosities of the Bi-Pb-Sb-Sr-Ca-Cu-O material by the spray pyrolysis technique. The morphology and hollow size in the porous superconducting material as well as the grain size in CdS and the morphology of the surface of the composite were obtained by Scanning Electron Microscopy. We obtained the critical superconducting temperature of both the Bi-Pb-Sb-Sr-Ca-Cu-O and the Bi-Pb-Sb-Sr-Ca-Cu-O/CdS composite measuring the resistivity. Both show a metallic behaviour just above the superconducting transition. For the superconductor alone, resistivity starts falling at Tc,on sup = 99,9 K and reaches zero at Tc,sup=76,3 K. The behaviour of the composite is different. The transition starts at Tc,on comp = 65,3 K and reaches zero resistance at Tc,comp = 56,5 K. This seems to indicate that the semiconductor penetrates the whole superconducting Bi-Pb-Sb-Sr-Ca-Cu-O sample so that there is no region of pure superconducting material left. Since the materials do not actually mix (see text) the behaviour might be attributable to the interface. Also the resistivity curves present a very interesting feature, i.e., below the temperature at which the composite attains zero-resistivity, a re-entrant behaviour manifests itself and a finite resistivity peak appears. It increases to a certain value to drop back to zero at some temperature below. We comment further on this feature in the text.
△ Less
Submitted 31 December, 2010;
originally announced January 2011.