Larger grains in high-Tc superconductors synthesized by the solid-state reaction route
Authors:
D. M. Gokhfeld,
M. I. Petrov,
S. V. Semenov,
A. D. Balaev,
I. V. Nemtsev,
A. D. Vasiliev,
M. S. Molokeev
Abstract:
Solid-state synthesis is widely used in exploratory research to study various structural modifications that affect the properties (critical temperature, critical current density, irreversibility field, etc.) of superconductors. The popularity of this method is due to its relative simplicity and availability of the necessary equipment. Combining solid-state synthesis and top-seeded melt growth allo…
▽ More
Solid-state synthesis is widely used in exploratory research to study various structural modifications that affect the properties (critical temperature, critical current density, irreversibility field, etc.) of superconductors. The popularity of this method is due to its relative simplicity and availability of the necessary equipment. Combining solid-state synthesis and top-seeded melt growth allows us to increase the grain size in a Tm- and Nd-based 1-2-3 superconductor. Samples with a grain size up to 0.1 mm have been obtained. X-ray diffraction, scanning electron microscopy and magnetization measurements have been used for investigating this superconducting material. The magnetization width ΔM has increased significantly in the synthesized samples. However the temperature dependence of the intragrain critical current density and the pinning force scaling give evidences that the pinning mechanism in the obtained superconductor is essentially the same as in polycrystalline superconductors synthesized by standard solid-state technology. The increase in grain size in the synthesized samples is the main reason for the high values of ΔM.
△ Less
Submitted 2 March, 2025; v1 submitted 11 December, 2024;
originally announced December 2024.
Conductivity, weak ferromagnetism and charge instability in $α-MnS$ single crystal
Authors:
S. S. Aplesnin,
L. I. Ryabinkina,
G. M. Abramova,
O. B. Romanova,
A. M. Vorotynov,
D. A. Velikanov,
N. I. Kiselev,
A. D. Balaev
Abstract:
The temperature dependence of resistivity, magnetization and electron-spin resonance of the $α- MnS $ single crystal were measured in temperature range of $5 K < T < 550 K$. Magnetization hysteresis in applied magnetic field up to 0.7 T at $T=5 K, 77 K, 300 K$, irreversible temperature behavior of magnetization and resistivity were found . The obtained data were explained in terms of degenerate…
▽ More
The temperature dependence of resistivity, magnetization and electron-spin resonance of the $α- MnS $ single crystal were measured in temperature range of $5 K < T < 550 K$. Magnetization hysteresis in applied magnetic field up to 0.7 T at $T=5 K, 77 K, 300 K$, irreversible temperature behavior of magnetization and resistivity were found . The obtained data were explained in terms of degenerate tight binding model using random phase approximation. The contribution of holes in $t_{2g}$ and $e_g$ bands of manganese ions to the conductivity, optical absorbtion spectra and charge instability in $α-MnS $ were studied. Charge susceptibility maxima resulted from the competition of the on-site Coulomb interaction between the holes in different orbitals and small hybridization of sub-bands were calculated at $T=160 K, 250 K, 475 K$.
△ Less