Inactive Overhang in Silicon Anodes
Authors:
Aidin I. OBrien,
Stephen E. Trask,
Devashish Salpekar,
Seoung-Bum Son,
Alison R. Dunlop,
Gabriel M. Veith,
Wenquan Lu,
Brian J. Ingram,
Daniel P. Abraham,
Andrew N. Jansen,
Marco-Tulio F. Rodrigues
Abstract:
Li-ion batteries contain excess anode area to improve manufacturability and prevent Li plating. These overhang areas in graphite electrodes are active but experience decreased Li+ flux during cycling. Over time, the overhang and the anode portions directly opposite to the cathode can exchange Li+, driven by differences in local electrical potential across the electrode, which artificially inflates…
▽ More
Li-ion batteries contain excess anode area to improve manufacturability and prevent Li plating. These overhang areas in graphite electrodes are active but experience decreased Li+ flux during cycling. Over time, the overhang and the anode portions directly opposite to the cathode can exchange Li+, driven by differences in local electrical potential across the electrode, which artificially inflates or decreases the measured cell capacity. Here, we show that lithiation of the overhang is less likely to happen in silicon anodes paired with layered oxide cathodes. The large voltage hysteresis of silicon creates a lower driving force for Li+ exchange as lithium ions transit into the overhang, rendering this exchange highly inefficient. For crystalline Si particles, Li+ storage at the overhang is prohibitive, because the low potential required for the initial lithiation can act as thermodynamic barrier for this exchange. We use micro-Raman spectroscopy to demonstrate that crystalline Si particles at the overhang are never lithiated even after cell storage at 45 oC for four months. Since the anode overhang can affect the forecasting of cell life, cells using silicon anodes may require different methodologies for life estimation compared to those used for traditional graphite-based Li-ion batteries.
△ Less
Submitted 15 May, 2024;
originally announced May 2024.
-
Pouch cells with 15% silicon calendar-aged for 4 years
Authors:
Marco-Tulio F. Rodrigues,
Zhenzhen Yang,
Stephen E. Trask,
Alison R. Dunlop,
Minkyu Kim,
Fulya Dogan,
Baris Key,
Ira Bloom,
Daniel P. Abraham,
Andrew N. Jansen
Abstract:
Small amounts of high-capacity silicon-based materials are already used in the anode of commercial Li-ion batteries, helping increase their energy density. Despite their remarkable storage capability, silicon continuously reacts with the electrolyte, accelerating time-dependent cell performance fade. Nevertheless, very limited information is available on the specific consequences of this reactivit…
▽ More
Small amounts of high-capacity silicon-based materials are already used in the anode of commercial Li-ion batteries, helping increase their energy density. Despite their remarkable storage capability, silicon continuously reacts with the electrolyte, accelerating time-dependent cell performance fade. Nevertheless, very limited information is available on the specific consequences of this reactivity for the calendar aging of Li-ion cells. Here, we analyze aging effects on 450 mAh pouch cells containing 15 wt% of Si (and 73 wt% graphite) after storage at 21 oC for four years. We show that severe losses of Si capacity occurred due to particle isolation when cells were stored at high states of charge (SOC), but not when cells were fully discharged prior to storage. Impedance rise was also significantly higher when cells were kept at high SOCs and was mostly due to phenomena taking place at the cathode; the continuous electrolyte reduction at the anode did not lead to a major increase in bulk electrode resistance. A series of post-test characterization provided additional information on the effects of time and SOC on the calendar aging of Si-containing cells. Our study highlights the many challenges posed by Si during calendar aging and can inform future studies in the field.
△ Less
Submitted 31 August, 2022;
originally announced September 2022.
-
Stress Evolution in Lithium-ion Composite Electrodes during Electrochemical Cycling and Resulting Internal Pressures on the Cell Casing
Authors:
Siva P. V. Nadimpalli,
Vijay A. Sethuraman,
Daniel P. Abraham,
Allan F. Bower,
Pradeep R. Guduru
Abstract:
Composite cathode coatings made of a high energy density layered oxide (Li1.2Ni0.15Mn0.55Co0.1O2, theoretical capacity ~377 mAh/g), polyvinylidene fluoride (PVdF) binder, and electron-conduction additives, were bonded to an elastic substrate. An electrochemical cell, built by pairing the cathode with a capacity-matched graphite anode, was electrochemically cycled and the real-time average stress e…
▽ More
Composite cathode coatings made of a high energy density layered oxide (Li1.2Ni0.15Mn0.55Co0.1O2, theoretical capacity ~377 mAh/g), polyvinylidene fluoride (PVdF) binder, and electron-conduction additives, were bonded to an elastic substrate. An electrochemical cell, built by pairing the cathode with a capacity-matched graphite anode, was electrochemically cycled and the real-time average stress evolution in the cathode coating was measured using a substrate-curvature technique. Features in the stress evolution profile showed correlations with phase changes in the oxide, thus yielding data complementary to in situ XRD studies on this material. The stress evolution showed a complex variation with lithium concentration suggesting that the volume changes associated with phase transformations in the oxide are not monotonically varying functions of lithium concentration. The peak tensile stress in the cathode during oxide delithiation was approximately 1.5 MPa and the peak compressive stress during oxide lithiation was about 6 MPa. Stress evolution in the anode coating was also measured separately using the same technique. The measured stresses are used to estimate the internal pressures that develop in a cylindrical lithium-ion cell with jelly-roll electrodes.
△ Less
Submitted 8 November, 2015;
originally announced November 2015.
-
Stress Evolution in Composite Silicon Electrodes during Lithiation/Delithiation
Authors:
Vijay A. Sethuraman,
Annam Nguyen,
Michael J. Chon,
Siva P. V. Nadimpalli,
Hailong Wang,
Daniel P. Abraham,
Allan F. Bower,
Vivek B. Shenoy,
Pradeep R. Guduru
Abstract:
We report real-time average stress measurements on composite silicon electrodes made with two different binders [Carboxymethyl cellulose (CMC), and polyvinylidene fluoride (PVDF)] during electrochemical lithiation and delithiation. During galvanostatic lithiation at very slow rates, the stress in a CMC-based electrode becomes compressive and increases to 70 MPa, where it reaches a plateau and incr…
▽ More
We report real-time average stress measurements on composite silicon electrodes made with two different binders [Carboxymethyl cellulose (CMC), and polyvinylidene fluoride (PVDF)] during electrochemical lithiation and delithiation. During galvanostatic lithiation at very slow rates, the stress in a CMC-based electrode becomes compressive and increases to 70 MPa, where it reaches a plateau and increases slowly thereafter with capacity. The PVDF-based electrode exhibits similar behavior, although with lower peak compressive stress of about 12 MPa. These initial experiments indicate that the stress evolution in a Si composite electrode depends strongly on the mechanical properties of the binder. Stress data obtained from a series of lithiation/delithiation cycles suggests plasticity induced irreversible shape changes in contacting Si particles, and as a result, the stress response of the system during any given lithiation/delithiation cycle depends on the cycling history of the electrode. While these results constitute the first in-situ stress measurements on composite Si electrodes during electrochemical cycling, the diagnostic technique described herein can be used to assess the mechanical response of a composite electrode made with other active material/binder combinations.
△ Less
Submitted 18 August, 2013;
originally announced August 2013.
-
Real-Time Stress Measurements in Lithium-ion Battery Negative-electrodes
Authors:
Vijay A. Sethuraman,
Nathan Van Winkle,
Daniel P. Abraham,
Allan F. Bower,
Pradeep R. Guduru
Abstract:
Real-time stress evolution in a graphite-based lithium-ion battery negative-electrode during electrolyte wetting and electrochemical cycling is measured through wafer-curvature method. Upon electrolyte addition, the composite electrode rapidly develops compressive stress of the order of 1-2 MPa due to binder swelling; upon continued exposure, the stress continues to evolve towards an apparent plat…
▽ More
Real-time stress evolution in a graphite-based lithium-ion battery negative-electrode during electrolyte wetting and electrochemical cycling is measured through wafer-curvature method. Upon electrolyte addition, the composite electrode rapidly develops compressive stress of the order of 1-2 MPa due to binder swelling; upon continued exposure, the stress continues to evolve towards an apparent plateau. During electrochemical intercalation at a slow rate, the compressive stress increases with the electrode's state-of-charge, reaching a maximum value of 10 - 12 MPa. There appears to be an approximate correlation between the rate of stress rise and the staging behavior of the lithiated graphite. De-intercalation at a slow rate results in a similar linear decrease in electrode stress. Tensile stress of a few MPa develops at the end of deintercalation in the first few cycles, after which the electrode remains under compressive stress only. Although higher peak stresses are seen at high C-rates, the dependence appears to be relatively weak (up to 5C). These measurements reveal, for the first time, the nature of stress evolution in practical lithium-ion-battery electrodes and provide useful data to quantify the driving force for mechanical damage that accrues in composite electrodes upon repeated cycling. While the reported results can serve as reference for calibrating theoretical and computational models to predict electrode stress and damage evolution, the methodology demonstrated can be used to measure stresses and characterize fatigue damage in any composite lithium-ion-battery electrode as well as optimize its microstructure to mitigate stress-related damage mechanisms.
△ Less
Submitted 10 January, 2012;
originally announced January 2012.